Waste PET textiles were glycolytica

Waste PET textiles were glycolytically degraded by ethylene gly- col and chemical recycling into flame-retardant rigid PUFs. The cellular structures of the PUFs were approximately homogene- ous spherical. DMMP was doped to improve the flame retard- ance of PUFs. The foam density decreased with the increasing of the blowing agent, distilled water, while the porosity increased. The doped DMMP decreased the foam density because of the partial rupture of the cell walls. The compression properties decreased while the weight ratio of DMMP increased. The LOI of PUFs without doped DMMP, 23.27–25.38% while changing the weight ratio of distilled water or catalyst, indicated the flame retardance of PUFs, which produced from recycle PET textile waste. The increasing ratio of doped DMMP into the PUFs increased the LOI to 27.69% and decreased after flame time from 32 to 14 s.

Kết quả (Việt) 2:

Dệt PET chất thải đã được phân hủy bởi glycolytically ethylene col gly- và tái chế chất hóa học vào PUFs cứng chống cháy. Các cấu trúc tế bào của PUFs là khoảng homogene- độc hại hình cầu. DMMP được pha tạp để cải thiện những ngọn lửa retard- ance của PUFs. Mật độ bọt giảm với sự gia tăng của các đại lý thổi, nước cất, trong khi độ xốp tăng. Các DMMP pha tạp làm giảm mật độ bọt vì vỡ một phần của thành tế bào. Các thuộc tính nén giảm trong khi tỷ lệ trọng lượng của DMMP tăng. Các LỢI của PUFs mà không pha tạp DMMP, 23,27-25,38% trong khi thay đổi tỷ lệ trọng lượng của nước cất hoặc chất xúc tác, chỉ ra các retardance ngọn PUFs, trong đó sản xuất từ ​​rác thải PET dệt. Tỷ lệ tăng của pha tạp DMMP vào PUFs tăng LOI đến 27,69% và giảm thời gian sau khi ngọn lửa 32-14 s.