Preparation of mesoporous adsorbent

Preparation of mesoporous adsorbent
Highly ordered mesoporous silica, MCM-41, was prepared
following the synthesis method described elsewhere.21 For the
preparation of Cu–Fe/MCM-41, CuCl (Aldrich, $99%) and FeCl2
(Aldrich, 98%) were utilized as received. Typically, 0.88 g CuCl
and 1.12 g of FeCl2 were dissolved in 125 ml of 2MHCl solution.
Aer this, 4.0 g of calcined MCM-41 was added into this
precursor solution and stirred for 1 h at room temperature.
Subsequently, the solvent was removed at 323 K for 12 h using a
rotary evaporator, and nally Fe–Cu/MCM-41 was dried in a
vacuum oven at room temperature for 3 days. For comparison,
Cu/MCM-41 and Ag/MCM-41 were prepared through the same
impregnation method described above, except that 2.0 g of CuCl
and 2.0 g of AgCl were loaded on MCM-41, respectively.

Kết quả (Việt) 2:

Chuẩn bị vật liệu hấp phụ mao
cao ra lệnh silica mao, MCM-41, đã được chuẩn bị
theo phương pháp tổng hợp mô tả elsewhere.21 Đối với những
chuẩn bị của Cu-Fe / MCM-41, CuCl (Aldrich, $ 99%) và FeCl2
(Aldrich, 98%) được sử dụng như là nhận được. Thông thường, 0,88 g CuCl
và 1,12 g FeCl2 được hòa tan trong 125 ml dung dịch 2MHCl.
Aer này, 4,0 g nung MCM-41 đã được bổ sung vào điều này
giải pháp tiền chất và khuấy trong 1 giờ ở nhiệt độ phòng.
Sau đó, các dung môi đã được gỡ bỏ tại 323 K cho 12 h sử dụng một
thiết bị bay hơi quay, và nally Fe-Cu / MCM-41 đã được sấy khô trong
lò chân không ở nhiệt độ phòng trong 3 ngày. Để so sánh,
Cu / MCM-41 và Ag / MCM-41 đã được chuẩn bị thông qua cùng một
phương pháp ngâm tẩm mô tả ở trên, ngoại trừ 2,0 g của CuCl
và 2,0 g AgCl được nạp vào MCM-41, tương ứng.