Bands for the entire series of 3d t

Bands for the entire series of 3d transition metals are presented in Fig. 16.4, which shows

narrow d bands crossing the wider s—p bands. The 3d bands are much broader than the 4f

bands of the lanthanides, but narrow enough to indicate that many atomic—like properties

carry over to the solid. At the end of the series is the noble metal Cu in which the d

bands are filled, but only slightly below the Fermi energy, which leads to its closed-shell,

non—magnetic behavior, and its yellow color. The transition metals have partially occupied

d bands. This leads to their magnetic behavior and correlations among the d electrons.

Nevertheless, independent-particletype methods are in many ways adequate to describe the

basic properties of these metals [132], e.g. the prediction of magnetism from the Stoner

criterion, as illustrated in Fig. 2.7 [107, 134, 132]. The total energies are remarkably well

described by the local density approximation, as illustrated in Fig. 2.3.

Kết quả (Việt) 2:

Bands cho toàn bộ loạt các kim loại chuyển tiếp 3d được trình bày trong hình. 16,4, trong đó cho thấy d dải hẹp băng qua dải s-p rộng hơn. Các ban nhạc 3d là rộng hơn nhiều so với 4f ban nhạc của các nguyên tố nhóm Lantan, nhưng đủ hẹp để chỉ ra rằng nhiều chất nguyên tử giống như thực hiện qua chất rắn. Vào cuối của loạt bài là Cu kim loại quý trong đó d ban nhạc được lấp đầy, nhưng chỉ hơi thấp hơn năng lượng Fermi, dẫn đến đóng vỏ, nó hành vi không từ tính, và màu vàng của nó. Các kim loại chuyển tiếp đã phần nào chiếm d ban nhạc. Điều này dẫn đến tính chất từ của họ và mối tương quan giữa các điện tử d. Tuy nhiên, phương pháp độc lập particletype là trong nhiều cách thích hợp để mô tả các đặc tính cơ bản của các kim loại này [132], ví dụ như các dự đoán của từ tính từ Stoner tiêu chí, như minh họa trong hình . 2.7 [107, 134, 132]. Tổng năng lượng được đáng kể cũng được mô tả bởi mật độ xấp xỉ địa phương, như minh họa trong hình. 2.3.