Fibre Morphology and PropertiesRami

Fibre Morphology and Properties

Ramie fibres are single cell systems, they are usually found as bundles of these single fibres, also called ultimates or ultimate fibres, and are cemented together within the plant stem. The fibres are located in the cortex layer of the stem just underneath the thin outer bark. The fibres are held together by natural cementing materials, such as resins and gums and the middle lamella. In bast fibres, the bast layer originates and develops from the terminal meristem close to the growing tip and is in its early development stage it is multinucleated and rich in protoplasm. It dissolves some of the middle lamella and develops simultaneously in length and diameter. This mechanism leads to pack the ultimate together tightly in polygonal form in cross section and oriented along longitudinal bundles with tapered ends. Due to its light packing, the middle lamella between the cells forms a thin uniform unbroken lamina (film) which covers each ultimate cell.

The microscopical observation of the topographical structure of the fibres reveals comparable structures with the other bust fibres. A comparison of various parameters of ramie and related natural fibres, such as jute,
cotton fibres has been given in the Table-1. Ramie also has the highest value of length and breadth ratio. It is also reported that the diameter (thin) of ramie fibres is lower than those of other natural fibres except kapok
[7]. Pic.-4 Cross sectional view of ramie fibre

The properly degummed fibres are single cell structures, length and breadth vary from 600-200 mm (average 120 mm) and 11-80 µm (average 50 µm) respectively. Depending on the variety of the species, agricultural practices, environmental conditions, soils and methods of decortications, the dimensions of the cells vary in considerable rate. As decorticated ramie is progressively degummed, (i) the tenacity of the fibre increases, (ii) the increase in the wet strength becomes higher (in the wet state, degumming ramie is about 30% stronger than what it is at 65% R. H.),
(iv) the fibre becomes more extensible, (v) capacity for absorption of moisture decreases, (vi) the fibre dries out at a quicker rate, (vii) the fibre gradually separates into individual cells and (viii) the fibre to fibre friction becomes lower [8].

Kết quả (Việt) 1:

Hình thái sợi và thuộc tínhVải gai sợi là hệ thống tế bào duy nhất, họ thường được tìm thấy như bó của các sợi duy nhất, cũng được gọi là ultimates hoặc sợi cuối cùng, và bê tông với nhau trong gốc thực vật. Các sợi được đặt tại các lớp vỏ của các thân cây chỉ bên dưới vỏ cây bên ngoài mỏng. Các sợi được tổ chức với nhau bằng vật liệu cementing tự nhiên, chẳng hạn như nhựa và nướu răng và phiến kính trung. Trong sợi lanh, lớp lanh có nguồn gốc và phát triển từ mô phân sinh thiết bị đầu cuối gần Mẹo ngày càng tăng và là trong giai đoạn phát triển đầu đó là multinucleated và phong phú trong vận. Nó hòa tan một số phiến kính trung và phát triển cùng một lúc trong chiều dài và đường kính. Cơ chế này dẫn đến đóng gói cuối cùng với nhau chặt chẽ trong các hình thức đa giác trong cắt ngang và định hướng dọc theo chiều dọc bó với giảm dần kết thúc. Do của nó đóng gói ánh sáng, các phiến kính trung giữa các tế bào tạo thành một mỏng thống nhất không gián đoạn phiến (phim) nằm trên một mỗi tế bào cuối cùng.Các quan sát microscopical cấu trúc địa hình của các sợi tiết lộ các cấu trúc so sánh với các sợi phá sản khác. Một so sánh của các thông số khác nhau của gai và liên quan đến các loại sợi tự nhiên, chẳng hạn như đay,bông sợi đã được đưa ra trong bảng 1. Vải gai cũng có giá trị cao nhất của tỷ lệ chiều dài và chiều rộng. Nó cũng được báo cáo rằng đường kính (mỏng) của sợi gai là thấp hơn so với các loại sợi tự nhiên khác ngoại trừ bông gòn[7]. Pic.-4 Cross sectional view of ramie fibreThe properly degummed fibres are single cell structures, length and breadth vary from 600-200 mm (average 120 mm) and 11-80 µm (average 50 µm) respectively. Depending on the variety of the species, agricultural practices, environmental conditions, soils and methods of decortications, the dimensions of the cells vary in considerable rate. As decorticated ramie is progressively degummed, (i) the tenacity of the fibre increases, (ii) the increase in the wet strength becomes higher (in the wet state, degumming ramie is about 30% stronger than what it is at 65% R. H.),(iv) the fibre becomes more extensible, (v) capacity for absorption of moisture decreases, (vi) the fibre dries out at a quicker rate, (vii) the fibre gradually separates into individual cells and (viii) the fibre to fibre friction becomes lower [8].

Kết quả (Việt) 2:

Fibre hình thái học và Properties sợi gai là hệ thống tế bào duy nhất, chúng thường được tìm thấy như bó của các loại sợi duy nhất, còn gọi là ultimate hay sợi cuối cùng, và được gắn kết với nhau trong thân cây. Các sợi được đặt trong lớp vỏ của thân cây chỉ bên dưới lớp vỏ mỏng bên ngoài. Các sợi được tổ chức với nhau bằng vật liệu xi măng tự nhiên, như nhựa và nướu răng và phiến kính trung. Trong các loại xơ libe, các lớp bắt nguồn libe và phát triển từ các mô phân sinh thiết bị đầu cuối gần đầu phát triển và đang trong giai đoạn phát triển ban đầu của nó là đa nhân và phong phú về nguyên sinh vật. Nó hòa tan một số phiến kính trung bình và phát triển đồng thời chiều dài và đường kính. Cơ chế này dẫn đến đóng gói cuối cùng với nhau chặt chẽ trong hình thức đa giác trong mặt cắt ngang và hướng dọc bó dọc với đầu nhọn. Do bao gói ánh sáng của nó, các phiến kính trung gian giữa các tế bào tạo thành một phiến lá không gián đoạn đồng phục mỏng (phim) mà bao gồm mỗi tế bào cuối cùng. Các quan sát kính hiển vi của cấu trúc địa hình của các sợi tiết lộ cấu trúc so sánh với các loại sợi khác phá sản. Một so sánh các thông số khác nhau của gai và sợi tự nhiên có liên quan, chẳng hạn như sợi đay, sợi bông đã được đưa ra trong Bảng 1. Ramie cũng có giá trị cao nhất của chiều dài và chiều rộng tỷ lệ. Nó cũng báo cáo rằng đường kính (mỏng) của sợi gai là thấp hơn so với các loại sợi tự nhiên khác, ngoại trừ bông gạo [7]. Pic.-4 chéo cắt của sợi gai Các sợi đúng tách keo là các cấu trúc tế bào đơn, chiều dài và chiều rộng khác nhau 600-200 mm (trung bình 120 mm) và 11-80 mm (trung bình 50 mm) tương ứng. Tùy thuộc vào sự đa dạng của các loài, nông nghiệp, điều kiện môi trường, đất và phương pháp của decortications, kích thước của các tế bào khác nhau về tỷ lệ đáng kể. Như gai decorticated đang dần tách keo, (i) sự kiên cường của các tăng chất xơ, (ii) sự gia tăng sức mạnh ướt trở nên cao hơn (trong trạng thái ẩm ướt, gai degumming là mạnh hơn so với những gì nó là 65% RH khoảng 30%) , (iv) các sợi trở nên mở rộng hơn, (v) năng lực hấp thu giảm độ ẩm, (vi) các sợi khô ra với một tốc độ nhanh hơn, (vii) các sợi dần dần tách thành các tế bào riêng lẻ và (viii) các sợi chất xơ ma sát trở nên thấp hơn [8].