( trang 32 ) Compounds in RRhSn ser

( trang 32 ) Compounds in RRhSn series show interesting magnetic properties. LaRhSn is a superconductor with TC=2 K [301]. CeRhSn shows valence fluctuation and highly anisotropic behavior as shown by single crystal study [302]. A strong enhancement in the heat capacity and magnetic susceptibility data below 7 K in this compound was observed, which was reported to arise due to the presence of unquenched moments in the quasi-Kagome lattice of Ce-Rh plane [302]. Some reports show that CeRhSn exhibits non-Fermi liquid behavior. The results obtained for CeRhSn can be interpreted in terms of Griffiths phase [303, 304]. Results obtained by Higaki et al. [305] for CeRhSn are slightly different for those reported earlier. They found that 4f electrons in CeRhSn have a localized nature. The elastic modulii and specific heat suggest that crystal field effect plays an important role, instead of Kondo effect. Subsequent to this, there have been many reports [306, 307, 308, 309, 310, 311], which give a detailed report on CeRhSn.
Compounds TbRhSn, DyRhSn, ErRhSn and TmRhSn show AFM ordering at low temperatures, while PrRhSn, SmRhSn, HoRhSn and NdRhSn show FM ordering [312, 313, 314, 315]. Mihalik et al. studied single crystals of NdRhSn and reported that at 9.8 K, a transition from paramagnetic to AFM state takes place, which has narrow temperature interval and goes to a FM like state, which has spontaneous magnetization and is about 2/3 of the value of free Nd3+ moment [316]. Such behavior in NdRhSn may be due to crystal field effects or complex magnetic structure of ground state [316]. Later, a detailed report on NdRhSn appeared, which shows that NdRhSn has FM ground state (Tt=7.6 K), which is followed by an incommensurate AFM state between TN=9.8 and Tt with moments aligned along easy magnetization axis, which is c-axis in both the magnetic states [317]. It has been reported that the magnetic phase transitions temperatures mentioned above in NdRhSn are sensitive to hydrostatic and uniaxial pressures. In a recent report, SmRhSn is shown to exhibit two magnetic transitions; one from paramagnetic to FM (at 14.5 K) and other at 7 K [315]. GdRhSn shows non-collinear magnetic ordering as seen from dc and ac magnetization as well as 155Gd Mössbauer spectroscopy studies [318]. Very recently, we observed that there is a sharp transition in the inverse magnetic susceptibility data at 245 K [80], which is also confirmed by heat capacity data. The low temperature XRD reveals that this transition is iso- structural.

Kết quả (Việt) 1:

(trang 32) Các hợp chất trong loạt RRhSn Hiển thị các tính chất thú vị từ. LaRhSn là một chất siêu dẫn với TC = 2 K [301]. CeRhSn cho thấy sự biến động của valence và cao đẳng hướng hành vi như được hiển thị bằng cách nghiên cứu tinh thể duy nhất [302]. Tăng cường mạnh mẽ ở nhiệt dung và dữ liệu nhạy cảm từ dưới 7 K trong hợp chất này được quan sát thấy, mà đã được báo cáo để phát sinh do sự hiện diện của các khoảnh khắc unquenched trong lưới quasi Kagome Ce-Rh bay [302]. Một số báo cáo cho thấy rằng CeRhSn trưng bày hành vi lỏng-Fermi. Kết quả thu được cho CeRhSn có thể được giải thích về giai đoạn Griffiths [303, 304]. Kết quả thu được bởi Higaki et al. [305] cho CeRhSn là hơi khác nhau cho các báo cáo trước đó. Họ thấy rằng 4f electron trong CeRhSn có một tính chất địa phương. Modulii đàn hồi và nhiệt đề nghị crystal lĩnh vực hiệu quả đóng một vai trò quan trọng, thay vì có hiệu lực Kondo. Sau này, đã có nhiều báo cáo [306, 307, 308, 309, 310, 311], mà cung cấp cho một báo cáo chi tiết về CeRhSn.Compounds TbRhSn, DyRhSn, ErRhSn and TmRhSn show AFM ordering at low temperatures, while PrRhSn, SmRhSn, HoRhSn and NdRhSn show FM ordering [312, 313, 314, 315]. Mihalik et al. studied single crystals of NdRhSn and reported that at 9.8 K, a transition from paramagnetic to AFM state takes place, which has narrow temperature interval and goes to a FM like state, which has spontaneous magnetization and is about 2/3 of the value of free Nd3+ moment [316]. Such behavior in NdRhSn may be due to crystal field effects or complex magnetic structure of ground state [316]. Later, a detailed report on NdRhSn appeared, which shows that NdRhSn has FM ground state (Tt=7.6 K), which is followed by an incommensurate AFM state between TN=9.8 and Tt with moments aligned along easy magnetization axis, which is c-axis in both the magnetic states [317]. It has been reported that the magnetic phase transitions temperatures mentioned above in NdRhSn are sensitive to hydrostatic and uniaxial pressures. In a recent report, SmRhSn is shown to exhibit two magnetic transitions; one from paramagnetic to FM (at 14.5 K) and other at 7 K [315]. GdRhSn shows non-collinear magnetic ordering as seen from dc and ac magnetization as well as 155Gd Mössbauer spectroscopy studies [318]. Very recently, we observed that there is a sharp transition in the inverse magnetic susceptibility data at 245 K [80], which is also confirmed by heat capacity data. The low temperature XRD reveals that this transition is iso- structural.

Kết quả (Việt) 2:

(Trang 32) Các hợp chất trong RRhSn loạt chương trình từ tính thú vị. LaRhSn là chất siêu dẫn với TC = 2 K [301]. CeRhSn hiện sự biến động hóa trị và hành vi có dị hướng như thể hiện trong nghiên cứu tinh duy nhất [302]. Một cải tiến mạnh mẽ ở nhiệt dung và dữ liệu nhạy cảm từ dưới 7 K trong hợp chất này đã được quan sát, được báo cáo phát sinh do sự hiện diện của những khoảnh khắc unquenched trong mạng quasi-Kagome của Ce-Rh máy bay [302]. Một số báo cáo cho thấy CeRhSn thể hiện hành vi chất lỏng không Fermi. Các kết quả thu được cho CeRhSn có thể được giải thích về Griffiths giai đoạn [303, 304]. Kết quả thu được bằng cách Higaki et al. [305] cho CeRhSn là hơi khác nhau đối với những báo cáo trước đó. Họ phát hiện ra rằng các điện tử 4f trong CeRhSn có tính chất địa phương. Các modulii đàn hồi và nhiệt cụ thể cho thấy rằng hiệu ứng trường tinh thể đóng một vai trò quan trọng, thay vì hiệu ứng Kondo. Tiếp theo đây, đã có nhiều báo cáo [306, 307, 308, 309, 310, 311], trong đó cung cấp một báo cáo chi tiết về CeRhSn.
Các hợp chất TbRhSn, DyRhSn, ErRhSn và TmRhSn chương AFM đặt ở nhiệt độ thấp, trong khi PrRhSn, SmRhSn , HoRhSn và NdRhSn chương trình FM đặt hàng [312, 313, 314, 315]. Mihalik et al. nghiên cứu tinh duy nhất của NdRhSn và báo cáo rằng ở 9,8 K, một quá trình chuyển đổi từ thuận từ trạng thái AFM diễn ra, trong đó có khoảng nhiệt độ hẹp và đi đến một FM như nhà nước, trong đó có từ hóa tự phát và khoảng 2/3 giá trị của tự do Nd3 + thời điểm [316]. Những hành động đó trong NdRhSn có thể là do hiệu ứng trường tinh thể hoặc cấu trúc từ tính phức tạp của các trạng thái cơ bản [316]. Sau đó, một báo cáo chi tiết về NdRhSn xuất hiện, trong đó cho thấy rằng NdRhSn có trạng thái cơ bản FM (Tt = 7,6 K), được theo sau bởi một nhà nước chưa tương xứng AFM giữa TN = 9,8 và Tt với những khoảnh khắc thẳng dọc theo trục từ hóa dễ dàng, đó là c- trục ở cả các quốc gia từ [317]. Nó đã được báo cáo rằng nhiệt độ chuyển pha từ nói trên trong NdRhSn rất nhạy cảm với áp lực thủy tĩnh và đơn trục. Trong một báo cáo gần đây, SmRhSn được hiển thị để triển lãm hai quá trình chuyển đổi từ; một từ thuận từ FM (14.5 K) và khác ở 7 K [315]. GdRhSn lãm sắp đặt từ phi thẳng hàng khi nhìn từ dc và ac từ hóa cũng như các nghiên cứu quang phổ 155Gd Mössbauer [318]. Rất gần đây, chúng tôi thấy rằng có một sự chuyển đổi mạnh trong các dữ liệu nhạy cảm từ nghịch đảo tại 245 K [80], mà còn được khẳng định bởi dữ liệu công suất nhiệt. Các XRD nhiệt độ thấp cho thấy rằng sự chuyển đổi này là ISO- cơ cấu.