When testing components compatibili

When testing components compatibility urea solution was heated with water at 126 °С until melting was complete. The ground ammonium sulphate was then added by small portions.
Magnesium oxide was then added into urea solution. Foam produced when stirring disappears in a short period of time. Considerable amount of insoluble particles are being presented in the solution. An increase of temperature to 133°С leads to boiling, further increase up to 137°С causes uncontrolled gas liquid mixture discharge from the tank.
The reaction of magnesium oxide suspension is weakly alkaline. Urea is hydrolyzed by acids and alkalis. The final products of alkaline hydrolysis will be urea and ammonia.
Infrared spectroscopic study of urea solution+maghesium oxide granulated material shows the presence of small amounts of magnesium cyanate. Thus, urea solution interact most likely with fine particles of magnesium oxide to give magnesium cyanate

Kết quả (Việt) 2:

Khi các bộ phận thử nghiệm giải pháp tương thích urê được đun nóng với nước ở 126 ° С đến khi nóng chảy đã được hoàn tất. Các sunphat amoni đất sau đó đã được bổ sung bởi các phần nhỏ.
Magnesium oxide sau đó đã được thêm vào dung dịch urê. Foam được sản xuất khi khuấy biến mất trong một khoảng thời gian ngắn. Số lượng đáng kể của các hạt không hòa tan đang được trình bày trong các giải pháp. Sự gia tăng của nhiệt độ đến 133 ° С dẫn đến sôi, tiếp tục tăng lên đến 137 ° С gây ra không kiểm soát được xả hỗn hợp lỏng khí từ bể.
Phản ứng của hệ thống treo magnesium oxide là yếu kiềm. Urea được thủy phân bằng axit và kiềm. Các sản phẩm cuối cùng của quá trình thủy phân kiềm sẽ là urê và amoniac.
Nghiên cứu quang phổ hồng ngoại của những giải pháp urê + maghesium oxit vật chất dạng hạt cho thấy sự hiện diện của một lượng nhỏ magiê cyanate. Vì vậy, giải pháp urê tương tác nhiều khả năng với các hạt mịn của magnesium oxide để cung cấp cho magiê cyanate