a b s t r a c tPolyurethane (PU) co

a b s t r a c t
Polyurethane (PU) composite foams were prepared by pour method with soy-based polyol (soyol). Foams
were tested for the evaluation of mechanical properties and cell morphologies as a portion of wood fiber
present. Thermal behaviors as well as foam morphology were investigated. Scanning electron microscopy
results exhibited that PU composite foam had improved cell size due to the presence of wood fiber. Thermalgravimetricanalysisanddifferentialscanningcalorimetryresultsclearlyshowedthemostsubstantial
increase of the glass transition temperature (Tg) and decrease of the decomposition temperature (Td) in
the fiber reinforced PU foam. PU composite foam had no influence on compressive strength; however,
it had caused slight reduction in tensile strength. PU composite foam displayed a broad distribution of
inter-domain spacing associating with morphological changes

Kết quả (Việt) 1:

một s b t r c tBọt polyurethane (PU) hỗn hợp đã được chuẩn bị bằng phương pháp đổ với soy-dựa polyol (soyol). Xà phòngđã được thử nghiệm cho việc đánh giá tính chất cơ học và tế bào morphologies như là một phần của sợi gỗhiện nay. Hành vi nhiệt cũng như bọt hình Thái đã được điều tra. Kính hiển vi điện tử quétkết quả trưng bày PU composite bọt đã cải thiện kích thước tế bào do sự hiện diện của chất xơ gỗ. Thermalgravimetricanalysisanddifferentialscanningcalorimetryresultsclearlyshowedthemostsubstantialtăng nhiệt độ chuyển đổi thủy tinh (Tg) và giảm nhiệt độ phân hủy (Td)sợi gia cường PU xốp. PU composite bọt có không có ảnh hưởng đến cường độ nén; Tuy nhiên,nó đã gây ra giảm nhẹ trong căng sức mạnh. PU composite bọt sẽ hiển thị một phân phối rộng củakhoảng cách giữa hai miền, kết hợp với những thay đổi về hình Thái