All samples were ultramicrotomed wi

All samples were ultramicrotomed with a diamond
knife on a Leica Ultracut UCT microtome (Bannockburn,
IL) at either room temperature (cyanate esters
and PS) or at 110°C (PPgMA and PA-6) to give
sections with a nominal thickness of 70 nm. The sections
were transferred from water (room temperature)
or dry conditions (110°C) to carbon-coated 200-mesh
Cu grids. Bright-field TEM images of PLSNs (except
for PA-6) were obtained at 120 kV, under low-dose
conditions, with a Philips 400T electron microscope
and with Kodak SO-161 film. Low-magnification images
were taken at 2,800 and 10,000. High-magnifi-
cation images were taken at 28,000 and 60,000.
Bright-field TEM images of PA-6 nanocomposites
were obtained at 120 kV, under low-dose conditions,
with a Philips CM-12 electron microscope, and were
digitally imaged with a charge coupled device (CCD)
camera

Kết quả (Việt) 2:

Tất cả các mẫu được ultramicrotomed với một viên kim cương
dao trên Microtome Leica Ultracut UCT (Bannockburn,
IL) ở hai nhiệt độ phòng (este cyanate
và PS) hoặc tại 110 ° C (PPgMA và PA-6) để cung cấp cho
các phần với độ dày danh nghĩa của 70 nm. Các phần
đã được chuyển giao từ nước (nhiệt độ phòng)
hoặc điều kiện khô (110 ° C) đến 200-lưới carbon bọc
Cu lưới. Hình ảnh TEM Bright-lĩnh vực PLSNs (ngoại trừ
cho PA-6) được thực hiện tại 120 kV, dưới liều thấp
điều kiện, với một kính hiển vi điện tử Philips 400T
và với Kodak SO-161 phim. Hình ảnh Low-phóng đại
được chụp tại 2.800 và 10.000 ?. Cao magnifi-
hình ảnh cation được chụp tại 28.000 và 60.000 ?.
ảnh TEM Bright trường của PA-6 nanocomposites
được thực hiện tại 120 kV, trong điều kiện liều thấp,
với một kính hiển vi điện tử Philips CM-12, và được
chụp ảnh kỹ thuật số với một Charge Coupled thiết bị (CCD)
camera