Today, diamond-coated cutting tools

Today, diamond-coated cutting tools are used primarily for machining non-ferrous materials such as aluminium-silicon alloys,
copper alloys, fibre-reinforced polymers, green ceramics and graphite. The tool life of cemented carbide cutting tools is greatly
improved by diamond coating, and typically more than 10 times the tool life is obtained. In this report we will present cutting
performances of diamond-coated inserts, twist drills, square end mills and ball nose end mills.
Diamond films are usually deposited more than 10 J.U11 thick to make tool life longer, since tool life is directly related to film
thickness. However, increased film thickness caused many problems with cutting performance. The most severe problem was the
decrease in the transverse rupture strength of the diamond-coated substrates. Because of this effect, the diamond-coated insert
used under high speed and intermittent cutting conditions was supposed to suffer chipping easily.

Kết quả (Việt) 2:

Hôm nay, công cụ cắt kim cương tráng được sử dụng chủ yếu cho các vật liệu kim loại màu công như hợp kim nhôm-silicon,
hợp kim đồng, polyme sợi cốt thép, gốm sứ màu xanh lá cây và than chì. Cuộc đời công cụ của các công cụ cắt cacbua củng được rất nhiều
cải thiện bằng lớp phủ kim cương, và thường là nhiều hơn 10 lần so với cuộc sống công cụ thu được. Trong báo cáo này, chúng tôi sẽ trình bày cắt
màn trình diễn của chèn kim cương tráng, khoan xoay, nhà máy cuối cùng vuông và nhà máy cuối cùng bóng mũi.
phim kim cương thường được gửi dày hơn 10 J.U11 để làm cho cuộc sống công cụ lâu hơn, kể từ khi cuộc sống là công cụ có liên quan trực tiếp để quay phim
dày. Tuy nhiên, tăng độ dày màng gây ra nhiều vấn đề với hiệu suất cắt. Vấn đề nghiêm trọng nhất là
giảm sức mạnh vỡ ngang của chất nền kim cương tráng. Do hiệu ứng này, chèn kim cương tráng
sử dụng theo tốc độ cao và điều kiện cắt liên tục được cho là bị sứt mẻ một cách dễ dàng.