Lee et al. [91] synthesised novel c

Lee et al. [91] synthesised novel composite electrolyte membranes consisting of 1-ethyl-3-methylimidazoliumfluorohy-drogenates ([EMIm](FH)nF) ionic liquids and the fluorinated poly-mers poly(decaflouorobiphenyl-(hexafluoropropylidene)diphenol)(s-DFBP-HFDP) and P(VDF-co-HFP). The ionic conductivity of the composite membrane P(VDF-co-HFP)/s-DFBPHFDP/[EMIm](FH)2.3F
with a weight ratio of 1/0.3/1.75 was 3.47102Scm1 at 1301C. A single fuel cell exhibited an OCV of approximately 1 V at 1301C for over 5 hours. The polarisation curves under dry gases at 1201C
were registered, showing a maximum power density of approximately 20.2 mW cm2 at 60.1 mA cm2
. Martinelli et al. [15]

Kết quả (Việt) 1:

Lee et al. [91] tổng hợp chất điện phân hỗn hợp tiểu thuyết màng bao gồm 1-etyl-3-methylimidazoliumfluorohy-drogenates ([EMIm](FH)nF) ion chất lỏng và các fluorinated poly-mers poly(decaflouorobiphenyl-(hexafluoropropylidene)diphenol)(s-DFBP-HFDP) và P(VDF-co-HFP). Độ dẫn điện ion của màng tế hỗn hợp P(VDF-co-HFP)/s-DFBPHFDP / [EMIm] (FH) 2.3Fvới trọng lượng tỉ lệ 1/0.3/1.75 là 3.47 102Scm 1 ở 1301C. Một tế bào nhiên liệu duy nhất trưng bày một OCV khoảng 1 V ở 1301C cho hơn 5 giờ. Các đường cong polarisation theo khí khô ở 1201Cđã được đăng ký, Hiển thị một mật độ năng lượng tối đa khoảng 20.2 mW cm 2 tại 60.1 mA cm2. Martinelli et al. [15]