Take a 6” length of armor, cut into

Take a 6” length of armor, cut into ½” lengths and place it in a polyethylene titration dish.
Drop several drops of Iron Sulfide Detection Solution on the armor. Foaming will occur if the zinc coating is still present on the armor wire.
If bright yellow precipitate (arsenic sulfide) is formed, iron sulfide is present on the armor.
If the sample is so oil wet that the detecting solution cannot penetrate it, add a few drop of DRILFOAM to water wet the sample. If the sample is paraffin coasted, heed may have to be applied to obtain a test.
Wash and dry the titration dish. Store the articles back in the box.

Test Results:
The presence of Iron Sulfide on the surface of the armor wire can confirm that the cable has been exposed to hydrogen sulfide and therefore is likely to have suffered H2S damage. The absence of a detectable iron sulfide on the surface is not proof, however, that the cable was not exposed to H2S.

Kết quả (Việt) 1:

Có một 6" chiều dài của vỏ giáp, cắt thành ½" độ dài và đặt nó trong một món ăn chuẩn độ bằng polyethylene.Thả một vài giọt giải pháp phát hiện sulfua sắt bộ giáp. Khuynh hướng tạo bọt sẽ xảy ra nếu mạ kẽm là vẫn còn hiện diện trên dây áo giáp.Nếu sáng màu vàng precipitate (asen sulfua) được thành lập, sulfua sắt là hiện nay trên áo giáp.Nếu mẫu do đó, dầu ướt giải pháp phát hiện không thể xâm nhập nó, thêm một vài giọt DRILFOAM để nước ngập mẫu. Nếu mẫu là parafin xeo, chú ý có thể cần phải được áp dụng để có được một bài kiểm tra.Rửa sạch và khô món ăn chuẩn độ. Lưu trữ các bài viết trở lại trong hộp.Kiểm tra kết quả:Sự hiện diện của sulfua sắt trên bề mặt của dây áo giáp có thể xác nhận rằng cáp đã được tiếp xúc với sulfua hiđrô và do đó có thể đã bị hư hại H2S. Sự vắng mặt của sulfua sắt phát hiện trên bề mặt không phải là bằng chứng, Tuy nhiên, cáp đã không tiếp xúc với H2S.