The Cu-C3N4 electrocatalysts descri

The Cu-C3N4 electrocatalysts described here were synthesized
through a one-step self-assembly procedure. Typically, dicyandiamide (12 mmol) was uniformly mixed with copper(II) chloride
(1.2 mmol). The resulting mixture was then heated at 500 ◦C in a
tube furnace for 5 h under N2 atmosphere. After cooling to room temperature, the final solid product (Cu-doped g-C3N4) was collected without further purification. This material was found to
contain 0.31 mmol of Cu in it, and it was thus designated as 0.31CuC3N4. Similarly, another material was synthesized in the same way,
but by decreasing the amount of copper(II) chloride to 0.85 mmol.
This sample was found to have 0.12 mmol Cu, and it was, therefore, labeled as the 0.12Cu-C3N4. For comparison, pure g-C3N4 was
also prepared by direct heating dicyandiamide in the absence of
copper(II) chloride.

Kết quả (Việt) 2:

Các điện xúc tác Cu-C3N4 mô tả ở đây được tổng hợp
thông qua một quy trình tự lắp ráp một bước. Thông thường, dicyandiamide (12 mmol) đã thống nhất với hỗn hợp đồng (II) clorua
(1.2 mmol). Hỗn hợp sau đó được nung nóng ở 500 ◦C trong một
lò ống cho 5 h dưới N2 khí quyển. Sau khi làm lạnh đến nhiệt độ phòng, các sản phẩm rắn cuối cùng (Cu-doped g-C3N4) được thu thập mà không cần tinh chế thêm. Tài liệu này đã được tìm thấy
có chứa 0,31 mmol của Cu trong nó, và do đó nó đã được chỉ định là 0.31CuC3N4. Tương tự như vậy, một vật liệu khác đã được tổng hợp trong cùng một cách,
nhưng bằng cách giảm lượng đồng (II) clorua 0,85 mmol.
Mẫu này được tìm thấy có 0,12 mmol Cu, và nó đã được, do đó, gắn nhãn là 0.12Cu-C3N4. Để so sánh, tinh khiết g-C3N4 được
cũng chuẩn bị bởi dicyandiamide nóng trực tiếp trong sự vắng mặt của
đồng (II) clorua.