HJ431 is a kind of smelting-type,re

HJ431 is a kind of smelting-type,red brown to light yellow colored,glassy granulated flux with high manganese and silicon but low fluorine,mesh 8-14(2.5-1.5mm),8-40(2.5-0.45mm) and 14-40(1.5-0.45mm). Either alternating or direct current can be used and Welding wires must be connected with the positive electrode when direct current is used. The welding technology has good performance.
Usage:
When applied to welding wires such as H08A,H08MnA and H10MnSi,it can weld low-carbon steel and some low-alloy steel like 16Mn and 15MnV,as well as ships,boilers and high-pressure vessels. And it also can be used for electro-slag and copper welding.
Cautions:
1.The oil soil,moisture,iron rust and other foreign substances must be removed from the surface before welding.
2.The flux must be baked under 300-400℃ for 2 hours.

Kết quả (Việt) 2:

HJ431 là một loại luyện kim loại, màu nâu đỏ đến vàng nhạt màu, thủy tinh thông lượng hạt với lượng mangan cao và silicon nhưng flo thấp, lưới 8-14 (2.5-1.5mm), 8-40 (2.5-0.45mm) và 14 -40 (1.5-0.45mm). Hoặc xen kẽ hoặc trực tiếp hiện tại có thể được sử dụng và dây hàn phải được kết nối với điện cực dương khi trực tiếp hiện tại được sử dụng. Các công nghệ hàn có hiệu suất tốt.
Cách sử dụng:
Khi áp dụng cho dây hàn như H08A, H08MnA và H10MnSi, nó có thể hàn thép carbon thấp và một vài thép hợp kim thấp như 16Mn và 15MnV, cũng như tàu, nồi hơi và áp suất cao tàu. Và nó cũng có thể được sử dụng cho điện xỉ và hàn đồng.
Thận trọng:
đất dầu 1.The, độ ẩm, gỉ sắt và các chất lạ khác phải được loại bỏ khỏi bề mặt trước khi hàn.
2.The thông phải được nướng dưới 300-400 ℃ trong 2 giờ.