Horseradish peroxidase (HPR) was us

Horseradish peroxidase (HPR) was used to catalyze the polymerization.Polyaniline was deposited on the surface of titanium dioxide NPs, forming a core-shell structure. Enzymatically synthesized nanocomposite was characterized by FT-IR spectroscopy, UV-Vis. Spectroscopy and scanning electron microscopy (SEM). The results indicate that a strong interaction exist at the interface of PANI and nano-titanium dioxide. The ability of PANI and PANI/Titanium dioxide NPs for electron exchange by Platinum (Pt) electrode, by casting the PANI and PANI/Titanium dioxide NPs on the Pt electrode surface was assessed by cyclic voltammetry. Difference of anodic and cathodic peak potential and formal potential values for PANI (281 mV and 425.5 mV, respectively) and PANI/Titanium dioxide NPs (39mV and 591.5 mV, respectively) were deduced by the analysis of voltammograms.

Kết quả (Việt) 2:

Cải ngựa peroxidase (HPR) đã được sử dụng để xúc tác polymerization.Polyaniline được lắng đọng trên bề mặt của titanium dioxide NP, tạo thành một cấu trúc core-shell. Enzym nanocomposite tổng hợp được đặc trưng bởi FT-IR, UV-Vis. Kính hiển vi quang phổ và vi điện tử quét (SEM). Kết quả cho thấy một sự tương tác mạnh mẽ tồn tại giao diện của Pani và nano-titanium dioxide. Khả năng của Pani và Pani / Titanium dioxide NP trao đổi electron của Platinum (Pt) điện cực, bằng cách đúc các Pani và Pani / Titanium dioxide NP trên bề mặt điện cực Pt được đánh giá bởi voltammetry cyclic. Sự khác biệt của anốt và giá trị tiềm năng tiềm năng và chính thức đỉnh cathodic cho Pani (281 mV và 425,5 mV, tương ứng) và Pani / Titanium dioxide NP (39mV và 591,5 mV, tương ứng) được suy ra bởi các phân tích của voltammograms.