This paper reports a study on pervious concrete made with Portland Pozzalona cement (PPC) as a binder. The mix
proportions were prepared with different coarse aggregate sizes. The size of coarse aggregate (CA) ranging from 6 mm to 12
mm was used in this study. Aggregate to binder ratio and water to binder ratio was considered as 3.3 and 0.35. Properties
such as compressive strength, flexural strength and permeability were examined and relationships between aggregate size vs
strength parameters, coefficient of permeability, void ratio and density properties of PPC binder pervious concrete were
drawn to evaluate the influence of CA sizes in pervious concrete. The results indicates that increase in aggregate size leads to
decrease in strength values and increase in permeability properties.
KEYWORDS Pervious concrete, Portland Pozzalona Cement (PPC), coarse aggregate, permeability, void ratio, density.

Kết quả (Việt) 1:

Bài báo này báo cáo một nghiên cứu về pervious bê tông được làm bằng xi măng Portland Pozzalona (PPC) như là một chất kết dính. Hỗn hợptỷ lệ đã được chuẩn bị với kích cỡ khác nhau thô tổng hợp. Kích thước của thô tổng hợp (CA) khác nhau, từ 6 mm đến 12mm được sử dụng trong nghiên cứu này. Tổng hợp tỷ lệ chất kết dính và nước để binder tỷ lệ được coi là 3,3 và 0,35. Thuộc tínhchẳng hạn như cường độ nén, flexural sức mạnh và tính thấm đã được kiểm tra và tổng hợp mối quan hệ giữa kích thước vsthông số sức mạnh, Hệ số thấm, hiệu tỉ lệ và mật độ tính chất của UBND tỉnh kết dính pervious bê tông đãrút ra để đánh giá ảnh hưởng của kích thước CA pervious bê tông. Kết quả cho thấy rằng sự gia tăng tổng hợp kích thước dẫn đếngiảm trong giá trị sức mạnh và tăng tính thấm.Từ khóa Pervious bê tông, xi măng Pozzalona Portland (PPC), thô tổng hợp, tính thấm, hiệu tỉ lệ, mật độ.