This agrees well with the conclusio

This agrees well with the conclusion in the simple analysis in Example 7.3, where
it was deduced that necking starts at a uniform strain of the specimen equal to
the strain-hardening exponent of the material. Hence, it is obvious that increasing
the strain-hardening exponent will improve formability in cases where necking
is the limiting phenomenon, because high-n-value delays the onset of necking. This
is why, for instance, extruded shapes are heat-treated into the T4 condition before
forming, even though this will increase the forming load. In the naturally aged T4
condition, the material has a high n-value (for instance, n = 0.25), and the onset of
necking is delayed in comparison with the soft annealed condition of the material
(n = 0.17). When necking starts, the material begins to thin out and cannot be
stretched further, to any extent, without fracturing. In sheet-metal forming neck

Kết quả (Việt) 1:

Điều này đồng ý với kết luận trong phân tích đơn giản trong ví dụ 7.3, nơi
nó được suy ra rằng necking bắt đầu từ một chủng thống nhất của mẫu vật bằng
số mũ căng thẳng-cứng của vật liệu. Do đó, nó là rõ ràng rằng ngày càng tăng
số mũ căng thẳng-cứng sẽ cải thiện formability trong trường hợp nơi necking
là hiện tượng hạn chế, bởi vì giá trị cao n trì hoãn sự khởi đầu của necking. Điều này
là lý do tại sao, ví dụ, tấm ép hình dạng được nhiệt vào tình trạng T4 trước khi
hình thành, mặc dù điều này sẽ làm tăng tải hình thành. Trong tự nhiên tuổi T4
tình trạng, các vật liệu có n-giá trị cao (ví dụ, n = 0,25), và sự khởi đầu của
necking trì hoãn so với điều kiện annealed mềm của vật liệu
(n = 0.17). khi necking bắt đầu, các tài liệu bắt đầu mỏng ra và không thể
kéo dài hơn nữa, đến mức độ nào, mà không bẻ gãy. Ở kim loại tấm hình thành cổ