The behaviour of (NH4)2V4`OP2O7, NH

The behaviour of (NH4)2V4`OP2O7, NH4V3`P2O7 and V3`(PO3)3 as catalysts in the ammoxidation of toluene and in the selective oxidation of n-butane has been studied by in situ EPR and catalytic measurements. In the first two samples an amorphous phase is formed under ammoxidation conditions which consists of e†ectively coupled VO2`ions and governs catalytic
performance. In the case of few isolated VO2`ions appear on the surface during toluene ammoxidation while coupled V(PO3)3,
VO2`ions are formed during n-butane oxidation. This catalyst was found to be inactive in the former but active in the latter
reaction. The di†erences in catalytic performance are explained in terms of the di†erent structure of the vanadium centres.

Kết quả (Việt) 2:

Các hành vi của (NH4) 2V4`OP2O7, NH4V3`P2O7 và V3` (PO3) 3 là chất xúc tác trong ammoxidation toluen và trong quá trình oxy hóa chọn lọc của n-butan đã được nghiên cứu bởi trong EPR tại chỗ và các phép đo xúc tác. Trong hai mẫu đầu tiên là pha vô định hình được hình thành trong điều kiện ammoxidation trong đó bao gồm e ?? VO2`ions một cách hiệu quả kết và điều chỉnh việc xúc tác
hiệu suất. Trong trường hợp một vài VO2`ions biệt xuất hiện trên bề mặt trong quá toluene ammoxidation trong khi cùng V (PO3) 3,
VO2`ions được hình thành trong quá trình oxy hóa n-butan. Chất xúc tác này đã được tìm thấy là không hoạt động trong các cựu nhưng hoạt động trong trường hợp sau
phản ứng. Các di ?? với hàm trong hoạt động xúc tác được giải thích về cấu trúc di ?? erent trong những trung tâm vanadi.