fig. 1 shows the XRD patterns of me

fig. 1 shows the XRD patterns of melt-spun Co80ÿxZr18CrxB2
(x = 0, 2, 3, and 4). The diffraction peaks of all the four samples
can be indexed as those of the single Co11Zr2 structure, in good
agreement with the report by Ivanova et al. [8]. In Fig. 2, we exhibit
the thermomagnetic curves of aforementioned samples. For each
sample, the curve presents only one magnetic transition that corresponds to Tc of Co11Zr2. This confirms that the as-spun Co80ÿxZr18-
Cr
xB2 (x = 0, 2, 3, and 4) ribbons are magnetically single-phase. It is
therefore concluded that the small addition of Cr does not alter the
phase composition of Co80Zr18B2. On the other hand, we establish
Tc
of Co11Zr2 for the sample with x = 0 to be 500 °C. The result

Kết quả (Việt) 2:

vả. 1 cho thấy các mẫu XRD của Co80ÿxZr18CrxB2 nóng chảy kéo thành sợi
(x = 0, 2, 3, và 4). Các đỉnh nhiễu xạ của tất cả bốn mẫu
có thể được lập chỉ mục như những cấu trúc Co11Zr2 duy nhất, ở tốt
nhất với báo cáo của Ivanova et al. [8]. Trong hình. 2, chúng ta biểu lộ
những đường cong thermomagnetic các mẫu nói trên. Đối với mỗi
mẫu, đường cong chỉ trình bày một quá trình chuyển đổi từ tương ứng với Tc của Co11Zr2. Điều này khẳng định rằng như-spun Co80ÿxZr18-
Cr
xB2 (x = 0, 2, 3, và 4) băng là từ tính một pha. Đó là
do đó kết luận rằng việc bổ sung nhỏ của Cr không làm thay đổi
thành phần pha của Co80Zr18B2. Mặt khác, chúng tôi thiết lập
Tc
của Co11Zr2 cho các mẫu với x = 0 là 500 ° C. Kết quả