Along with the Cl− ion, [C16mim]+ i

Along with the Cl− ion, [C16mim]+ ion will also be aligned and arrayed along the BiOCl layer driven by the Coulomb coupling force. It is reasonable to deduce that [C16mim]Cl, which is considered as a supramolecular solvent involved ordered structure, is selectively adsorbed on the (001) plane of BiOCl to effectively inhibit crystalline growth in the [001] direction. Therefore, the growth of BiOCl crystals are inhibited along the c-axis to form ultrathin BiOCl nanoflakes. Hereafter, Huang and co-workers reported a facile, one-pot approach to the uniform
BiOBr hollow microspheres in the ionic liquid precursor 1-hexadecyl-3-methylimidazolium bromide ([C16mim]Br).66. The possible formation mechanism is proposed in Fig. 5. Due to the limited miscibility of the ionic liquid precursor ([C16mim]Br) and co-solvent 2-methoxyethanol, micronized ionic liquid emulsions are formed under vigorous stirring, which are surrounded by 2-methoxyethanol containing Bi3+ ions.

Kết quả (Việt) 2:

Cùng với các ion Cl-, [C16mim] + ion cũng sẽ được liên kết và dàn trận cùng lớp BiOCl thúc đẩy bởi lực lượng khớp nối Coulomb. Đây là hợp lý để suy luận rằng [C16mim] Cl, được coi như một dung môi siêu phân tử liên quan đến cấu trúc lệnh, được chọn lọc hấp phụ trên (001) máy bay của BiOCl để ức chế hiệu quả tăng trưởng tinh thể trong [001] hướng. Do đó, sự tăng trưởng của các tinh thể BiOCl bị ức chế dọc theo c-trục để hình siêu mỏng BiOCl nanoflakes. Sau đây, Huang và đồng nghiệp báo cáo một facile, cách tiếp cận một nồi để thống nhất
BiOBr microspheres rỗng trong các ion tiền chất lỏng 1-hexadecyl-3-methylimidazolium bromide ([C16mim] Br) .66. Cơ chế hình thành có thể được đề xuất trong hình. 5. Do sự trộn lẫn hạn chế của tiền chất lỏng ion ([C16mim] Br) và đồng dung môi 2-methoxyethanol, Micronized nhũ tương lỏng ion được hình thành dưới khuấy mạnh mẽ, được bao bọc bởi 2-methoxyethanol chứa các ion Bi3 +.