Lee et al. [91] synthesised novel composite electrolyte membranes consisting of 1-ethyl-3-methylimidazoliumfluorohy-drogenates ([EMIm](FH)nF) ionic liquids and the fluorinated poly-mers poly(decaflouorobiphenyl-(hexafluoropropylidene)diphenol)(s-DFBP-HFDP) and P(VDF-co-HFP). The ionic conductivity of the composite membrane P(VDF-co-HFP)/s-DFBPHFDP/[EMIm](FH)2.3F with a weight ratio of 1/0.3/1.75 was 3.47102Scm1 at 1301C.
A single fuel cell exhibited an OCV of approximately 1 V at 1301C for over 5 hours. The polarisation curves under dry gases at 1201C were registered, showing a maximum power density of approxi-mately 20.2 mW cm2 at 60.1 mA cm2. Martinelli et al. [15] investigated the physical properties of proton conducting polymer membranes based on protic ionic liquids (EImTf2N) incorporated into a polymer matrix (PVDF-co-HFP).

Kết quả (Việt) 2:

Lee et al. [91] tổng hợp tiểu thuyết màng phức hợp điện gồm 1-etyl-3-methylimidazoliumfluorohy-drogenates ([EMIm] (FH) nF) chất lỏng ion và flo poly-Mers poly (decaflouorobiphenyl- (hexafluoropropylidene) diphenol) (s-DFBP- HFDP) và P (VDF-co-HFP). Độ dẫn ion của màng P composite (VDF-co-HFP) /-DFBPHFDP s / [EMIm] (FH) 2.3F với một tỷ lệ trọng lượng của 1 / 0,3 / 1,75 là 3,47? 102Scm? 1 ở 1301C.
Một nhiên liệu duy nhất tế bào trưng bày một OCV khoảng 1 V ở 1301C trong hơn 5 giờ. Các đường cong phân cực dưới khí khô ở 1201C đã đăng ký, cho thấy mật độ năng lượng tối đa xấp xỉ 20,2 mW-2 cm? Tại 60,1 mA cm2. Martinelli et al. [15] nghiên cứu các tính chất vật lý của proton tiến hành các màng polymer dựa trên chất lỏng ion proton (EImTf2N) kết hợp vào một ma trận polymer (PVDF-co-HFP).