Estrella et al. [36] also studied t

Estrella et al. [36] also studied the effect of 1500 mg/l of zero
valance metal NPs (Ag0
, Cu0 and Fe0
) on the AD of AGS. For
acetoclastic methanogenesis, Cu0 was found to completely inhibit
the methanogenesis, while Fe0 decreased the methanogenesis
activities to 85% and Ag0 showed no significant effect on methanogenesis
activities. For hydrogentrophic methanogenesis, the
results showed Cu0 to also completely inhibit the methanogenesis
while Fe0 to decrease the methanogenesis activities to 91% and Ag0
to have no significant effect on methanogenesis activities, see Fig
12 [36].
Positive effects on the AD and biogas production using metal
nano-substances were achieved by Al-Ahmad et al. [47]. They
studied the effect of metal NPs encapsulated in porous SiO2 on the
AD at 55 1C using 5 mg/l acetate substrate of concentration and
105 mol/l of Fe, Pd, Pt, Ni, Co, Ag and Cu NPs encapsulated in SiO2.
The results showed significant increase in methane production in
case of Ni (70%), Co (48%), Fe (7%) and Pt (6%) as shown in Fig. 20 a.
The authors confirmed the results by using different concentrations
of metal NPs (104 and 106 mol/l) where the higher
concentration (104 mol/l) showed a significant increase in
methane production as shown in Fig. 20a and b [47].
Nano-silver has also been widely investigated in the field of
biogas production. Yang et al. [48] studied the effect of nano-silver
(average size 21 nm) on biogas production from Municipal solid
waste (MSW) for 250 days. The addition of 1 and 10 mg/kg nanosilver
to the sludge resulted in the decrease of the methane
production to 90% and 20%, respectively, see Fig. 21 [48].
In another study, Yang et al. [49] studied the effect of moderate
nano-silver concentrations on the AD of mixture of digested sludge
and glucose for about 14 days under mesophilic and ambient conditions.
Five samples have been investigated; the negative control
sample without Ag NPs or glucose, the positive control sample
without Ag NPs, 10 mg Ag NPs/l, 40 mg Ag NPs/l and 40 mg Agþ/l.
The results showed the negative control sample to have a significant
decrease in methane production in comparison with the other
samples that showed equal productions, indicating that Ag NPs at
moderate concentrations had no significant effect on methane production,
see Fig. 22. The authors mentioned also the absence of Ag
ions release from Ag NPs during the AD process [49].
This was asserted by Garcia et al. [39] who studied the effect of
Au and Ag NPs (20, 30 nm in size) on the AD of waste sludge for 50
days under both mesophilic (37 1C) and thermophilic conditions
(55 1C), see Fig. 14. The results did not show any significant
difference in biogas production upon the addition of the 100 mg/
l Au or 170 mg/l Ag NPs [39].
Doolette et al. [50] studied the effect of Ag NPs on anaerobic
digestion of waste sludge. The Ag NPs as well as Agþ ions did not
show any change in methane production as shown in Fig. 23. These
results are in agreement with those reported by Garcia et al [39].

Kết quả (Việt) 1:

Estrella et al. [36] cũng nghiên cứu tác dụng của 1500 mg/l của zeroValance kim loại NPs (Ag0, Cu0 và Fe0) vào quảng cáo của công ty AGS. Choacetoclastic methanogenesis, Cu0 đã được tìm thấy để ức chế hoàn toànmethanogenesis, trong khi Fe0 giảm các methanogenesisCác hoạt động đến 85% và Ag0 cho thấy không có tác động đáng kể trên methanogenesishoạt động. Cho hydrogentrophic methanogenesis, cáckết quả cho thấy Cu0 cũng hoàn toàn ức chế các methanogenesistrong khi Fe0 để giảm các hoạt động methanogenesis 91% và Ag0có không có tác động đáng kể về methanogenesis hoạt động, xem hình12 [36].Các tác động tích cực vào quảng cáo và sản xuất khí sinh học bằng cách sử dụng kim loạiNano-chất đã đạt được bởi Al-Ahmad et al. [47]. Họnghiên cứu ảnh hưởng của kim loại NPs gói gọn trong xốp SiO2 trên cácQuảng cáo ở 55 1 c bằng cách sử dụng 5 mg/l axetat bề mặt của tập trung và105 mol/l của Fe, Pd, Pt, Ni, Co, Ag, Cu NPs gói gọn trong SiO2.Kết quả cho thấy sự gia tăng đáng kể trong sản xuất mêtantrường hợp của Ni (70%), Co (48%), Fe (7%) và Pt (6%) như minh hoạ trong hình 20 một.Các tác giả đã xác nhận kết quả bằng cách sử dụng nồng độ khác nhaucủa kim loại NPs (104 và 106 mol/l) nơi cao hơntập trung (104 mol/l) cho thấy một sự gia tăng đáng kể trongmêtan sản xuất như minh hoạ trong hình 20a và b [47].Nano-bạc cũng đã được rộng rãi nghiên cứu trong lĩnh vựcsản xuất khí sinh học. Yang et al. [48] nghiên cứu tác dụng của nano-bạc(trung bình kích thước 21 nm) trên khí sinh học sản xuất từ Municipal rắnwaste (MSW) for 250 days. The addition of 1 and 10 mg/kg nanosilverto the sludge resulted in the decrease of the methaneproduction to 90% and 20%, respectively, see Fig. 21 [48].In another study, Yang et al. [49] studied the effect of moderatenano-silver concentrations on the AD of mixture of digested sludgeand glucose for about 14 days under mesophilic and ambient conditions.Five samples have been investigated; the negative controlsample without Ag NPs or glucose, the positive control samplewithout Ag NPs, 10 mg Ag NPs/l, 40 mg Ag NPs/l and 40 mg Agþ/l.The results showed the negative control sample to have a significantdecrease in methane production in comparison with the othersamples that showed equal productions, indicating that Ag NPs atmoderate concentrations had no significant effect on methane production,see Fig. 22. The authors mentioned also the absence of Agions release from Ag NPs during the AD process [49].This was asserted by Garcia et al. [39] who studied the effect ofAu and Ag NPs (20, 30 nm in size) on the AD of waste sludge for 50days under both mesophilic (37 1C) and thermophilic conditions(55 1C), see Fig. 14. The results did not show any significantdifference in biogas production upon the addition of the 100 mg/l Au or 170 mg/l Ag NPs [39].Doolette et al. [50] studied the effect of Ag NPs on anaerobicdigestion of waste sludge. The Ag NPs as well as Agþ ions did notshow any change in methane production as shown in Fig. 23. These
results are in agreement with those reported by Garcia et al [39].

Kết quả (Việt) 2:

Estrella et al. [36] cũng đã nghiên cứu ảnh hưởng của 1500 mg / l của zero
NP viền bằng vải kim loại
(Ag0, Cu0 và
FE0) trên AD của AGS. Đối với
khí methan acetoclastic, Cu0 đã được tìm thấy để ức chế hoàn toàn
các khí methan, trong khi FE0 giảm khí methan
hoạt động đến 85% và Ag0 cho thấy không có ảnh hưởng đáng kể về khí methan
hoạt động. Đối với khí methan hydrogentrophic, các
kết quả cho thấy Cu0 để cũng hoàn toàn ức chế các khí methan
trong khi FE0 để giảm hoạt động khí methan đến 91% và Ag0
không có tác động đáng kể đến hoạt động khí methan, xem hình
12 [36].
Tác động tích cực trên AD và khí sinh học sản xuất sử dụng kim loại
nano-chất đã đạt được bằng Al-Ahmad et al. [47]. Họ
nghiên cứu ảnh hưởng của NP kim loại được đóng gói trong xốp SiO2 trên
AD tại 55 1C dùng 5 mg / l acetate chất nền của sự tập trung và
105 mol / l của Fe, Pd, Pt, Ni, Co, Ag, Cu NP gói gọn trong SiO2.
Kết quả cho thấy sự gia tăng đáng kể trong sản xuất methane trong
trường hợp của Ni (70%), Co (48%), Fe (7%) và Pt (6%) như hình. 20 a.
Các tác giả khẳng định các kết quả bằng cách sử dụng nồng độ khác nhau
của NP kim loại (104 và 106 mol / l), nơi cao hơn
nồng độ (104 mol / l) cho thấy một sự gia tăng đáng kể trong
sản xuất methane như thể hiện trong hình. 20a và b [47].
Nano bạc cũng đã được nghiên cứu rộng rãi trong các lĩnh vực
sản xuất khí sinh học. Yang et al. [48] ​​nghiên cứu ảnh hưởng của nano-bạc
(trung bình kích thước 21 nm) về sản xuất khí sinh học từ rắn thành phố
thải (MSW) cho 250 ngày. Việc bổ sung 1 và 10 mg / kg nanosilver
để bùn dẫn đến sự sụt giảm của methane
sản xuất tới 90% và 20%, tương ứng, xem hình. 21 [48].
Trong một nghiên cứu khác, Yang et al. [49] nghiên cứu ảnh hưởng của vừa phải
nồng độ nano bạc trên AD của hỗn hợp bùn tiêu hóa
và glucose trong khoảng 14 ngày trong điều kiện mesophilic và môi trường xung quanh.
Năm mẫu đã được điều tra; điều khiển âm
mẫu mà không có Ag NP hoặc glucose, các mẫu chứng dương
mà không Ag NP, 10 mg Ag NP / l, 40 mg Ag NP / l và 40 mg Agþ / l.
Kết quả cho thấy các mẫu kiểm soát tiêu cực để có một ý nghĩa
giảm trong sản xuất metan so với các khác
mẫu cho thấy sản phẩm tương đương, chỉ ra rằng Ag NP ở
nồng độ vừa phải không có ảnh hưởng đáng kể đến sản xuất methane,
xem hình. 22. Các tác giả cũng đề cập đến sự vắng mặt của Ag
ion phát hành từ Ag NP trong quá trình AD [49].
Điều này đã được khẳng định bởi Garcia et al. [39] đã nghiên cứu ảnh hưởng của
Au và Ag NP (20, 30 nm trong kích thước) trên AD của bùn thải cho 50
ngày dưới hai mesophilic (37 1C) và điều kiện ưa nhiệt
(55 1C), xem hình. 14. Kết quả không cho thấy bất kỳ ý nghĩa
khác biệt trong sản xuất khí sinh học vào việc bổ sung 100 mg /
l Au hoặc 170 mg / l Ag NP [39].
Doolette et al. [50] nghiên cứu ảnh hưởng của Ag NP trên kỵ khí
tiêu hóa của bùn thải. Các NP Ag cũng như các ion Agþ đã không
cho thấy bất kỳ thay đổi trong sản xuất methane như thể hiện trong hình. 23. Những
kết quả là trong thỏa thuận với những báo cáo của Garcia et al [39].