PROPERTY VALUE TEST METHODCountry o

PROPERTY VALUE TEST METHOD
Country of manufacture Germany
Membrane thickness (measured
without any adhesive or fleece
backing)
1.2 mm
Solids content (M. Wt. >100,000) >90% -
Bitumen resistance Yes DIN 16937
Vapour diffusion resistance 500 N/50mm DIN 53354
Elongation >300% DIN 53354
Puncture resistance drop height 600 mm SIA 280 Part 14

Kết quả (Việt) 1:

PROPERTY VALUE TEST METHODCountry of manufacture GermanyMembrane thickness (measuredwithout any adhesive or fleecebacking)1.2 mmSolids content (M. Wt. >100,000) >90% -Bitumen resistance Yes DIN 16937Vapour diffusion resistance <15,000 DIN 5312Fire resistance B2 DIN 4102Root resistance Root-proof FLLTensile strength >500 N/50mm DIN 53354Elongation >300% DIN 53354Puncture resistance drop height 600 mm SIA 280 Part 14

Kết quả (Việt) 2:

SỞ HỮU GIÁ TRỊ PHƯƠNG PHÁP THỬ
Nước sản xuất Đức
màng dày (đo
mà không cần bất kỳ chất dính hoặc lông cừu
bồi)
1.2 mm
nội dung chất rắn> 90% (M. Wt> 100.000.) -
Bitum kháng Có DIN 16.937
hơi kháng khuếch tán <15.000 DIN 5312
cháy kháng B2 DIN 4102
gốc kháng root-bằng chứng FLL
Độ bền kéo> 500 N / 50mm DIN 53.354
giãn dài> 300% DIN 53.354
thủng kháng giảm chiều cao 600 mm SIA 280 Phần 14