Figure 5 displays the number of bac

Figure 5 displays the number of bacterial colonies grown in
the presence of different amount of AgNO3 and spherical
nanoparticles when 100 l (approximately 105 CFU/ml) of
sample was applied to each plate. The results clearly indicate
that at a given concentration of silver, inhibition of bacterial
growth depends on the initial number of cells. An amount of 6
g of spherical nanoparticles almost completely prevented
bacterial growth (Fig. 5B). At silver (in the form of AgNO3)
amounts of 12.5 g and above, 100% inhibition of bacterial
growth was also observed (Fig. 5A). This is markedly different
from the results obtained when the initial number of bacterial
cells was 107 CFU. In this case also, the results, expressed as
log (1
x)  f(c), follow the first-order exponential decay
curve with a nonlinear regression coefficient (R2
) of 0.99
(Fig. 5).

Kết quả (Việt) 2:

Hình 5 hiển thị số khuẩn lạc vi khuẩn phát triển trong
sự hiện diện của số lượng khác nhau của AgNO3 và hình cầu
hạt nano khi 100? L (khoảng 105 CFU / ml) của
mẫu được áp dụng cho mỗi tấm. Kết quả chỉ ra rõ ràng
rằng ở một nồng độ nhất định của bạc, ức chế vi khuẩn
phát triển phụ thuộc vào số lượng ban đầu của các tế bào. Số tiền
6? G của các hạt nano hình cầu gần như hoàn toàn ngăn chặn
sự tăng trưởng của vi khuẩn (Hình. 5B). Tại bạc (ở dạng AgNO3)
số tiền là 12,5 g? Và ở trên, 100% ức chế các vi khuẩn
tăng trưởng cũng được quan sát (Hình. 5A). Điều này là khác nhau rõ rệt
từ các kết quả thu được khi số lượng ban đầu của vi khuẩn
tế bào là 107 CFU. Trong trường hợp này cũng có thể, kết quả, thể hiện như
log (1? X)? f (c), hãy làm theo các thứ tự đầu tiên phân rã theo hàm mũ
đường cong với một hệ số hồi quy phi tuyến
(R2) 0,99
(Fig. 5).