Figure 3 illustrates square-wave st

Figure 3 illustrates square-wave stripping voltammograms for cadmium and lead, at concentration
levels of 1 to 200 ppb in 0.1M HNO3 solutions, at the bismuth film electrode. As compared to the
mercury electrode, the shapes of electric current for varying the applied potentials at the bismuth
electrode were not symmetrical and the potentials causing peak currents were inconsistent. Such
problems might be related to the non-homogeneous distribution of the bismuth on the GC electrode
with varying sizes of the particles (Fig. 4). However, as found in the mercury film electrode tests, the
bismuth-coated electrodes showed strong linear relationships between concentrations of Cd and Pb
ranging from 1 to 200 ppb,and peak currents measured at around -0.7and -0.45 V for Cd and Pb ions,
respectively . Therefore, it was concluded that bismuth could be a viable candidate for detecting Cd and
Pb in the 0.1M HNO3 solutions.

Kết quả (Việt) 2:

Hình 3 minh họa sóng vuông tước voltammograms cho cadmium và chì, ở nồng
độ từ 1 đến 200 ppb trong HNO3 0,1M giải pháp, ở điện cực màng bismuth. Khi so sánh với các
điện cực thủy ngân, các hình dạng của dòng điện khác nhau cho các tiềm năng áp dụng tại bismuth
điện cực không đối xứng và tiềm năng gây ra các dòng cao điểm là không phù hợp. Như vậy
vấn đề có thể liên quan đến sự phân bố không đồng nhất của bismuth trên điện cực GC
với kích thước khác nhau của các hạt (Hình. 4). Tuy nhiên, như được tìm thấy trong các bài kiểm tra điện cực vàng màng thủy ngân, các
điện cực bismuth bọc cho thấy mối quan hệ tuyến tính chặt chẽ giữa nồng độ của Cd và Pb
trong khoảng từ 1 đến 200 ppb, và dòng cao điểm đo vào khoảng -0.7and -0,45 V cho các ion Cd và Pb ,
tương ứng. Vì vậy, có thể kết luận rằng bismuth có thể là một ứng cử viên khả thi để phát hiện Cd và
Pb trong các giải pháp HNO3 0,1M.