The ionic liquid uptake in the membrane was evaluated through the weight difference between the pristine and the impregnated membrane. The [HSO3-BBIm][TfO] and [HSO3-BMIm][Tf2N] uptakes were 9.4% and 1.6%, respectively. A higher current density was obtained when the Nafion membrane
was impregnated with [HSO3-BBIm][TfO], reaching 217 mA cm2 without humidifying the inlet gases at 251C. Di Noto and co-workers[85] studied the properties of Nafion 117 membranes doped with triethylammonium methanesulphonate (TMS) and triethylammonium perfluorobutanesulphonate (TPFBu). The water content of TPFBu is less than that of TMS due to its hydrophobicity, agreeing with the lower water content of Nafion doped with TPFBu relative to Nafion doped with TMS. The IL uptakes of the membranes impregnated with TMS and TPFBu were 20 and 39 wt%, respectively.

Kết quả (Việt) 2:

Sự hấp thụ chất lỏng ion trong màng được đánh giá thông qua các khác biệt trọng lượng giữa các nguyên sơ và màng ngâm tẩm. Các [HSO3-BBIm] [TFO] và [HSO3-BMIm] [Tf2N] uptakes là 9,4% và 1,6%, tương ứng. Một mật độ hiện tại cao hơn thu được khi màng Nafion
đã được ngâm tẩm với [HSO3-BBIm] [TFO], đạt 217 mA cm2 mà không ẩm khí đầu vào tại 251C. Di Noto và đồng nghiệp [85] nghiên cứu các tính chất của màng Nafion 117 pha tạp với triethylammonium methanesulphonate (TMS) và triethylammonium perfluorobutanesulphonate (TPFBu). Hàm lượng nước của TPFBu là ít hơn của TMS do sợ nước của mình, đồng ý với nội dung nước thấp hơn của Nafion pha tạp với TPFBu so với Nafion pha tạp với TMS. Các uptakes IL của màng ngâm tẩm với TMS và TPFBu là 20 và 39% khối lượng, tương ứng.