Characterization
The structural evolution of the gel species was tracked
down with high-resolution transmission electron micros-
copy (HRTEM), in a FEI-Philips CM300 microscope in
low-dose mode operating at 300 kV accelerating voltage,
equipped with a LaB6 electron gun and EDAX energy dis-
persive X-ray spectrometer (EDS). Samples were prepared
by diluting the suspension of the reaction products in dis-
tilled water, ultrasonicating them and depositing a drop
onto Cu grids coated with a thin (5 nm thickness) holey
carbon support film. In order to verify that the zeolite crys-
tals do not collapse under the high vacuum in the TEM
some of the samples were studied at liquid nitrogen temper-
ature using Gatan Inc. cryo-system, model 626. No appar-
ent increase in crystallinity or size distribution was
observed, which allowed us to conclude that utilization of
low-dose technique at room temperature is an adequate

Kết quả (Việt) 1:

Đặc tínhSự tiến hóa cơ cấu của các loài gel được theo dõixuống với độ phân giải cao truyền điện tử micros -sao chép (HRTEM), trong một kính hiển vi phi-Philips CM300 trongliều thấp chế độ hoạt động 300 kV thúc đẩy điện thế,được trang bị với một khẩu súng điện tử LaB6 và EDAX năng lượng dis-Máy đo phổ tia x persive (chủ biên). Mẫu đã chuẩn bị sẵn sàngbởi pha loãng đình chỉ các sản phẩm phản ứng ở dis-cày nước, ultrasonicating họ và thổi bụi giảmlên Cu lưới bọc mỏng (5 nm dày) holeyCarbon hỗ trợ film. Để xác minh rằng zeolite crys -tals không sụp đổ dưới chân không cao trong TEMmột số mẫu đã được nghiên cứu tại nitơ lỏng temper-ature sử dụng Gatan Inc cryo-hệ thống, mô hình 626. Không có appar-tai mũi họng gia tăng trong phân phối crystallinity hoặc kích thướcquan sát, cho phép chúng tôi kết luận rằng sử dụng cácliều thấp kỹ thuật ở nhiệt độ phòng là một đầy đủ