It has been proposed that a semicry

It has been proposed that a semicrystalline polymer consists of small crystalline
regions (crystallites), each having a precise alignment, which are interspersed with
amorphous regions composed of randomly oriented molecules. The structure of
the crystalline regions may be deduced by examination of polymer single crystals,
which may be grown from dilute solutions.These crystals are regularly shaped, thin
platelets (or lamellae), approximately 10 to 20 nm thick, and on the order of
10 m long. Frequently, these platelets will form a multilayered structure, like that
shown in the electron micrograph of a single crystal of polyethylene, Figure 14.11.
The molecular chains within each platelet fold back and forth on themselves, with
folds occurring at the faces; this structure, aptly termed the chain-folded model, is

Kết quả (Việt) 1:

Nó đã được đề xuất rằng một polymer semicrystalline bao gồm nhỏ tinh thểkhu vực (crystallites), mỗi có một sắp xếp chính xác, mà được xen kẽ vớivô định hình vùng gồm ngẫu nhiên theo định hướng các phân tử. Cấu trúc củacác khu vực tinh thể có thể được rút ra bởi các kiểm tra của các polyme tinh thể duy nhất,mà có thể được phát triển từ loãng giải pháp.Các tinh thể được thường xuyên hình, mỏngtiểu cầu (hoặc lá mỏng), khoảng 10-20 nm dày, và đặt hàng của10 m dài. Thường xuyên, các tiểu cầu sẽ tạo thành một cấu trúc multilayered, như thếHiển thị trong micrograph điện tử của một tinh thể duy nhất bằng polyethylene, con số 14,11.Các chuỗi phân tử trong tiểu cầu mỗi gấp lại trên chính mình, vớinếp gấp xảy ra tại khuôn mặt; cấu trúc này, được gọi là mô hình chuỗi-gấp, là