Herein, we study the contribution o

Herein, we study the contribution of urea-polymerized powder
(denoted as UCN) with an obvious porous structure to the photocatalytic activity. A facile one-stepsynthesis process is conducted in
the air without introducing an additional hard template. In
comparison, thiourea (urea derivative) and dicyandiamide (DCDA,
commonly used precursor) are also used as single sources under the
same pyrolysis reaction conditions (denoted as TCN and DCN). The
g-C3N4 powders all showed the characteristic graphitic-like layer
structures and repeating units. However, UCN possesses a high
Brunauer–Emmett–Teller (BET) surface area and an obviously
porous structure, which is a key step towards the photocatalytic H2
production from water on polymeric g-C3N4. This work clearly
presents a promising raw material and shows a new method for
optimizing semiconductor-based water splitting systems.

Kết quả (Việt) 1:

Ở đây, chúng tôi nghiên cứu sự đóng góp của bột urê-polymerized(biểu hiện như là UCN) với một cơ cấu xốp rõ ràng cho các hoạt động photocatalytic. Một quá trình một-stepsynthesis facile được tiến hành tạikhông khí mà không cần giới thiệu một mẫu cứng bổ sung. Ởso sánh, thiourea (urê phái sinh) và dicyandiamide (DCDA,thường được sử dụng tiền thân của) cũng được sử dụng như là nguồn duy nhất theo cácđồng nhiệt phân phản ứng điều kiện (biểu hiện như TCN và DCN). Cácg-C3N4 bột tất cả cho thấy lớp graphitic giống như đặc trưngcấu trúc và đơn vị lặp đi lặp lại. Tuy nhiên, UCN có một caoDiện tích bề mặt Brunauer-Emmett-rút tiền (đặt cược) và rõ ràngcấu trúc xốp, đó là một bước quan trọng hướng tới photocatalytic H2sản xuất từ nước trên polymer g-C3N4. Điều này làm việc rõ ràngtrình bày một nguyên liệu hứa hẹn và cho thấy một phương pháp mới nhấttối ưu hóa dựa trên bán dẫn nước chia hệ thống.