20.4 g of waste polystyrene was put

20.4 g of waste polystyrene was put in a bottom
glass flask reactor (500 cm 3) equipped with
mechanical agitation, vertical condenser, and
thermometer. The flask containing the solution was
heated in the silicone oil bath to 48— 52 °C. Acetyl
sulfate as sulfonating agent was prepared in a separate
flask: 12.0 cm 3 of acetic anhydride was added
carefully to 6.0 cm 3 of 95—97% sulfuric acid. The
prepared acetyl sulfate was poured through the
vertical condenser to the solution of WPSS resins. The
reaction mixture was heated to about 35 °C and stirred
for 1 h. Then the sulfonated WPS resins was isolated and
dried in oven for 24 h at 300C.

Kết quả (Việt) 1:

20,4 g của chất thải polystyrene được đặt trong một đáykính bình lò phản ứng (500 cm 3) được trang bị vớikích động cơ khí, ngưng tụ dọc, vànhiệt kế. Bình chứa các giải pháp làđun nóng trong bồn tắm dầu silicone để 48-52 ° C. Axetylsulfat như sulfonating đại lý đã được chuẩn bị trong một riêng biệtbình: 12,0 cm 3 axetic anhydrit đã được bổ sungcẩn thận để 6.0 cm 3 của 95-97% axít sulfuric. Cácchuẩn bị sẵn sàng axetyl sulfat được đổ thông qua cácngưng tụ dọc để các giải pháp của WPSS nhựa. Cácphản ứng hỗn hợp được đun nóng đến khoảng 35 ° C và khuấycho 1 h. Sau đó, các loại nhựa WPS sulfonated được cô lập vàkhô trong lò cho 24 h ở 300C.