2.2. Preparation of CS-PMAA nanopar

2.2. Preparation of CS-PMAA nanoparticles

The CS-PMAA nanoparticles were obtained by

polymerization of MAA in CS solution in a two step process [11]. In the first step, chitosan was dissolved in a 0.5% (v/v) methacrylic acid aqueous

solution for 12 h under magnetic stirring. The CS

concentration used in synthesis was 0.2% (w/v). In

the second step, 0.2 mmol of K2S2O8 was added to the solution with continued stirring, until the solution became clear. The polymerization was then

carried out at 70°C under magnetic stirring for 1 h

leading to the formation of CS-PMAA nanoparticles, which was then cooled in an ice bath.

Kết quả (Việt) 1:

2.2. chuẩn bị của hạt nano CS-PMAAHạt nano CS-PMAA đã đượctrùng hợp của MAA trong CS giải pháp trong một quá trình hai bước [11]. Trong bước đầu tiên, chitosan hòa tan trong axit methacrylic 0,5% (v/v) nướcgiải pháp cho 12 h theo từ khuấy. Các CStập trung được sử dụng trong tổng hợp là 0,2% (w/v). ỞBước thứ hai, 0.2 mmol của K2S2O8 đã được thêm vào các giải pháp với tiếp tục khuấy, cho đến khi các giải pháp trở nên rõ ràng. Sự trùng hợp là sau đóthực hiện tại 70° C theo từ khuấy cho 1 hdẫn đến sự hình thành của hạt nano CS-PMAA, sau đó được làm lạnh trong một bồn tắm băng.

Kết quả (Việt) 2:

2.2. Chuẩn bị CS-PMAA hạt nano của các hạt nano CS-PMAA đã thu được bằng phản ứng trùng hợp của MAA trong dung CS trong một quá trình hai bước [11]. Trong bước đầu tiên, chitosan được hòa tan trong một 0,5% (v / v) metacrylic dung dịch axit giải pháp cho 12 h dưới khuấy từ. Các CS tập trung được sử dụng trong tổng hợp là 0,2% (w / v). Trong bước thứ hai, 0,2 mmol của K2S2O8 đã được thêm vào dung dịch cùng với tiếp tục khuấy cho đến khi các giải pháp trở nên rõ ràng. Trùng hợp sau đó đã được thực hiện tại 70 ° C dưới khuấy từ cho 1 h dẫn đến sự hình thành của CS-PMAA hạt nano, mà sau đó được làm lạnh trong đá.