MATERIAL : AL (KS D 6006, ALDCS 12.

MATERIAL : AL (KS D 6006, ALDCS 12.1종)
2. AFTER DIE-CASTING, SHOULD BE NO HARMFUL ELEMENTS ON THE SURFACE
SUCH AS SINK MARK, WELD LINE, CRACK, CRAZING, WHITENING ETC.
3 DETAILS ABOUT THE MOLD SHALL BE DETERMINED BY CONSULTATION WITH THE DESIGNER.
: PARTING LINE, GATE, RUNNER, EJECTOR PIN, OVERFLOW ETC.
4. GENERAL DRAFT ANGLE : Max. 5°
5. AFTER FINISH, THE DEGREE OF GLOSS IS UNIFORM. AND SHOULD BE NO HARMFUL ELEMENTS
ON THE USE SUCH AS SWELLING, DESQUAMATION, ETC.
6. SHOULD BE NO HARMFUL ELEMENTS ABOUT PRODUCTS SUCH AS BURR, SCRATCH, BENDING, ETC.
7. GENERAL SPECIFICATION ON SUBSTANCE CONTROL REQUIREMENTS(KMWI-A51-B080)COMPLY WITH THE LATEST.

Kết quả (Việt) 1:

CHẤT LIỆU: AL (KS D 6006, ALDCS 12.1종)2. SAU KHI KIỆN ĐÚC, NÊN KHÔNG CÓ YẾU TỐ ĐỘC HẠI TRÊN BỀ MẶT CHẲNG HẠN NHƯ CHÌM MARK, HÀN KHỔ, NỨT, RẠN, WHITENING VV.3 THÔNG TIN CHI TIẾT VỀ CÁC KHUÔN MẪU ĐƯỢC XÁC ĐỊNH BỞI THAM KHẢO Ý KIẾN VỚI CÁC NHÀ THIẾT KẾ. : CHIA TAY DÒNG, GATE, Á HẬU, EJECTOR PIN, TRÀN VV.4. TỔNG dự THẢO GÓC: Max. 5°5. SAU KHI HOÀN TẤT, MỨC ĐỘ BÓNG LÀ ĐỒNG NHẤT. VÀ NÊN KHÔNG CÓ YẾU TỐ ĐỘC HẠI VỀ VIỆC SỬ DỤNG NHƯ SƯNG TẤY, DESQUAMATION, VV.6. NÊN KHÔNG CÓ YẾU TỐ ĐỘC HẠI VỀ SẢN PHẨM NHƯ BURR, ĐẦU, UỐN, VV.7. TỔNG ĐẶC ĐIỂM KỸ THUẬT VỀ CHẤT KIỂM SOÁT YÊU CẦU (KMWI-A51-B080) TUÂN THỦ CÁC MỚI NHẤT.

Kết quả (Việt) 2:

VẬT LIỆU: AL (KS D 6006, ALDCS 12.1 종)
2. SAU DIE-ĐÚC, NÊN KHÔNG CÓ YẾU TỐ GÂY HẠI TRÊN MẶT
NHƯ tản MARK, HÀN LINE, CRACK, crazing, WHITENING ETC.
3 CHI TIẾT VỀ CÁC MỐC SẼ ĐƯỢC ĐỊNH CỦA HIỆP VỚI DESIGNER.
: Chia tay LINE, GATE, RUNNER, PIN Ejector, OVERFLOW ETC.
4. DỰ THẢO CHUNG ANGLE: Max. 5 °
5. SAU FINISH, THE DEGREE HÀNH BÓNG LÀ UNIFORM. VÀ NÊN KHÔNG CÓ YẾU TỐ GÂY HẠI
VỀ VIỆC SỬ DỤNG như sưng, tróc vảy, ETC.
6. NÊN KHÔNG CÓ YẾU TỐ GÂY HẠI VỀ SẢN PHẨM NHƯ Burr, scratch, uốn, ETC.
7. ĐẶC CHUNG VỀ YÊU CẦU CHẤT CONTROL (KMWI-A51-B080) QUY MỚI NHẤT.