when the loading levels of P25 and

when the loading levels of P25 and 5 wt%
Ni/P25 increased to 4 mg/cm2, the SRs(8 h) of A. niger spores would
decrease to 0.844 ± 0.181 and 0.807 ± 0.194, respectively. The similar result was also found in the cases of 0.2 wt% Ag/P25 and 2 wt%
Cu/P25 catalysts.
The antifungal kinetics fitted the Chick-Watson model (firstorder decay model) [45]:
SR = exp(−kt) (3)
in which k is the inactivation rate constant; t is the elapsed time.
The fitting result of Eq. (3) is listed in Table 1. Accordingly, nanoCu supported TiO2 catalysts were better than nano-Ni supported
ones on the inactivation of A. niger spores, but worse than nano-Ag

Kết quả (Việt) 1:

khi nâng cấp P25 và 5 wt %Ni/P25 tăng lên 4 mg/cm2, bào tử SRs(8 h) A. niger nàogiảm đến 0.844 ± 0.181 và 0.807 ± 0.194, tương ứng. Kết quả tương tự cũng được tìm thấy trong các trường hợp cách 0.2 wt % Ag/P25 và 2 wt %Cu/P25 chất xúc tác.Kinetics kháng nấm trang bị mô hình gà-Watson (mô hình phân rã firstorder) [45]:SR = exp(−kt) (3)trong đó k là hằng số tỷ lệ ngừng hoạt động; t là thời gian.Kết quả phù hợp của Eq. (3) được liệt kê trong bảng 1. Theo đó, nanoCu hỗ trợ TiO2 chất xúc tác là tốt hơn so với hỗ trợ nano-Ninhững ngày ngừng hoạt động A. Niger bào tử, nhưng tồi tệ hơn nano-Ag

Kết quả (Việt) 2:

khi mức tải của P25 và 5% trọng lượng
Ni / P25 tăng lên đến 4 mg / cm2, SRS (8 h) của A. niger bào tử sẽ
giảm xuống còn 0,844 ± 0,181 và 0,807 ± 0,194, tương ứng. Kết quả tương tự cũng được tìm thấy trong các trường hợp là 0,2% khối lượng Ag / P25 và 2% trọng lượng
chất xúc tác Cu / P25.
Động học kháng nấm lắp mô hình Chick-Watson (mô hình firstorder sâu) [45]:
SR = exp (-kt) (3)
trong đó k là hằng số tốc độ; t là thời gian trôi qua.
Các kết quả phù hợp của phương trình. (3) được liệt kê trong Bảng 1. Theo đó, nanoCu hỗ trợ xúc tác TiO2 là tốt hơn so với nano-Ni hỗ trợ
những người trên bất hoạt của các bào tử A. niger, nhưng tệ hơn nano Ag