Control experiments under other con

Control experiments under other conditions were conducted to
have a better understanding about the formation process of the
product. As depicted in Fig. S1 and S2 (see ESI{), well-defined
SnO2 NS structures cannot be obtained at different concentrations
of either SnCl2 or NH4F. This indicates that the relative amount of
Sn2+ and F2 is an important factor that assures the formation of the desired structure. Time-series analysis (Fig. S3, ESI{) reveals
that after reaction for only 5 h irregular aggregates with sheet-like
subunits are formed. As the reaction prolongs to 10 h, the
nanosheet structure becomes more pronounced. After the reaction
for 30 h, the product contains rigid nanosheets with small size and
thickness. However, some broken structures can also be identified,
probably because the product cannot withstand the prolonged
hydrothermal treatment.

Kết quả (Việt) 2:

Thí nghiệm kiểm soát trong các điều kiện khác đã được tiến hành để
có một sự hiểu biết tốt hơn về quá trình hình thành của các
sản phẩm. Như mô tả trong hình. S1 và S2 (xem ESI {), được xác định rõ
cấu trúc SnO2 NS không thể có được ở các nồng độ khác nhau
của một trong hai SnCl2 hoặc NH4F. Điều này chỉ ra rằng số lượng tương đối của
SN2 + F2 và là một yếu tố quan trọng đảm bảo độ hình thành các cấu trúc mong muốn. Phân tích chuỗi thời gian (Hình. S3, ESI {) tiết lộ
rằng sau phản ứng chỉ trong 5 h uẩn không thường xuyên với tấm giống như
tiểu đơn vị được hình thành. Khi phản ứng xảy kéo dài đến 10 h, các
cấu trúc nanosheet trở nên rõ rệt hơn. Sau khi các phản ứng
trong 30 h, các sản phẩm có chứa nanosheets cứng với kích thước nhỏ và
độ dày. Tuy nhiên, một số cấu trúc bị hỏng cũng có thể được xác định,
có lẽ bởi vì sản phẩm không thể chịu được sự kéo dài
điều trị thủy nhiệt.