Urea (0.092 mol), phthalic anhydrid

Urea (0.092 mol), phthalic anhydride (0.018 mol), copper (II) chloride (0.005 mol), and ammonium molybdate (0.0596 mol) were ground for 30 min in an agate mortar. The mixture was put into aflask and wetted with distilled water (5 mL). It was then heated in a microwave oven at 600 W for 5 min. The crude product was purified by washing in sequence with hot water (70
C), 6 M HCl, 1 M NaOH, and with hot water again followed byfiltration. After these steps, the pigment was washed with ethanol andfiltered until thefiltrate was colorless. The resulting pigment was dried in an oven at 100
C

Kết quả (Việt) 1:

Urê (0.092 mol), phthalic anhydrit (0.018 mol), đồng (II) clorua (0.005 mol), và amoni molipđat (0.0596 mol) là mặt đất trong 30 phút trong một vữa agate. Hỗn hợp được đưa vào aflask và lên với nước cất (5 mL). Nó sau đó được đun nóng trong một lò nướng vi sóng tại 600 W cho 5 phút. Các sản phẩm dầu thô được tinh chế bằng cách rửa trong chuỗi với nước nóng (70 C), 6 M HCl, 1 M NaOH, và với nước nóng một lần nữa theo byfiltration. Sau khi các bước sau, các sắc tố được rửa sạch với cồn andfiltered cho đến khi thefiltrate là không màu. Các sắc tố kết quả khô trong một lò ở 100 C

Kết quả (Việt) 2:

Urea (0,092 mol), anhydrit phthalic (0,018 mol), đồng (II) clorua (0,005 mol), và ammonium molybdate (0,0596 mol) là mặt đất trong 30 phút trong một cối mã não. Hỗn hợp này được đưa vào aflask và ẩm với nước cất (5 ml). Sau đó nó được nung nóng trong lò vi sóng ở 600 W trong 5 phút. Các sản phẩm thô được tinh lọc bằng cách rửa liên tục với nước nóng (70? C), 6 M HCl, NaOH 1 M, và với nước nóng trở lại sau byfiltration. Sau khi các bước này, các sắc tố đã được rửa sạch bằng ethanol andfiltered cho đến thefiltrate là không màu. Các sắc tố kết quả được sấy khô trong lò ở 100 C?