Vickers Hardness TestingHardness is

Vickers Hardness Testing

Hardness is a characteristic of a material, not a fundamental physical property. It is defined as the resistance to indentation, and it is determined by measuring the permanent depth of the indentation. More simply put, when using a fixed force (load) and a given indenter, the smaller the indentation, the harder the material. Indentation hardness value is obtained by measuring the depth or the area of the indentation using one of over 12 different test methods. Click here to learn more about hardness testing basics.

The Vickers hardness test method, also referred to as a microhardness test method, is mostly used for small parts, thin sections, or case depth work. The Vickers method is based on an optical measurement system. The Microhardness test procedure, ASTM E-384, specifies a range of light loads using a diamond indenter to make an indentation which is measured and converted to a hardness value. It is very useful for testing on a wide type of materials as long as test samples are carefully prepared. A square base pyramid shaped diamond is used for testing in the Vickers scale. Typically loads are very light, ranging from a few grams to one or several kilograms, although "Macro" Vickers loads can range up to 30 kg or more. The Microhardness methods are used to test on metals, ceramics, composites - almost any type of material.

Since the test indentation is very small in a Vickers test, it is useful for a variety of applications: testing very thin materials like foils or measuring the surface of a part, small parts or small areas, measuring individual microstructures, or measuring the depth of case hardening by sectioning a part and making a series of indentations to describe a profile of the change in hardness. The Vickers method is more commonly used.

Sample preparation is usually necessary with a microhardness test in order to provide a small enough specimen that can fit into the tester. Additionally, the sample preparation will need to make the specimen’s surface smooth to permit a regular indentation shape and good measurement, and to ensure the sample can be held perpendicular to the indenter. Usually the prepared samples are mounted in a plastic medium to facilitate the preparation and testing. The indentations should be as large as possible to maximize the measurement resolution. (Error is magnified as indentation sizes decrease) The test procedure is subject to problems of operator influence on the test results.

Kết quả (Việt) 1:

Thử nghiệm độ cứng VickersĐộ cứng là một đặc tính của một tài liệu, không phải là một tính chất vật lý cơ bản. Nó được định nghĩa là các kháng để thụt lề, và nó được xác định bằng cách đo sâu thụt lề, vĩnh viễn. Hơn chỉ cần đặt, khi sử dụng một lực lượng cố định (tải) và một indenter nhất định, nhỏ hơn thụt lề, các khó hơn các tài liệu. Thụt lề độ cứng giá trị thu được bằng cách đo độ sâu hoặc khu vực thụt lề bằng cách sử dụng một phương pháp thử nghiệm khác nhau trên 12. Click vào đây để tìm hiểu thêm về độ cứng thử nghiệm khái niệm cơ bản.Phương pháp thử nghiệm độ cứng Vickers, cũng được gọi là một microhardness kiểm tra phương pháp, chủ yếu được sử dụng cho một phần nhỏ, phần mỏng, hoặc trường hợp sâu làm việc. Phương pháp Vickers dựa trên một hệ thống đo lường quang học. Các Microhardness kiểm tra thủ tục, ASTM E-384, chỉ định một loạt các ánh sáng tải bằng cách sử dụng một indenter kim cương để làm cho một indentation đo và chuyển đổi một giá trị của độ cứng. Nó là rất hữu ích để thử nghiệm trên một loại rộng của vật liệu miễn là thử nghiệm mẫu được chuẩn bị kỹ lưỡng. Một hình kim cương kim tự tháp vuông cơ sở được sử dụng để thử nghiệm ở quy mô Vickers. Thường tải là rất nhẹ, khác nhau, từ một vài gram để một hoặc một vài kg, mặc dù "Vĩ mô" Vickers tải có thể dao động lên đến 30 kg trở lên. Phương pháp Microhardness được sử dụng để thử nghiệm trên kim loại, gốm sứ, vật liệu tổng hợp - hầu như bất kỳ loại vật liệu.Since the test indentation is very small in a Vickers test, it is useful for a variety of applications: testing very thin materials like foils or measuring the surface of a part, small parts or small areas, measuring individual microstructures, or measuring the depth of case hardening by sectioning a part and making a series of indentations to describe a profile of the change in hardness. The Vickers method is more commonly used.Sample preparation is usually necessary with a microhardness test in order to provide a small enough specimen that can fit into the tester. Additionally, the sample preparation will need to make the specimen’s surface smooth to permit a regular indentation shape and good measurement, and to ensure the sample can be held perpendicular to the indenter. Usually the prepared samples are mounted in a plastic medium to facilitate the preparation and testing. The indentations should be as large as possible to maximize the measurement resolution. (Error is magnified as indentation sizes decrease) The test procedure is subject to problems of operator influence on the test results.

Kết quả (Việt) 2:

Vickers Hardness Testing Độ cứng là một đặc tính của một vật chất, không phải là một tài sản vật lý cơ bản. Nó được định nghĩa là khả năng chống thụt đầu dòng, và nó được xác định bằng cách đo độ sâu thường trực của indentation. Đơn giản hơn đặt, khi sử dụng một lực lượng cố định (load) và một indenter cho, nhỏ thụt đầu dòng, các khó hơn các vật liệu. Giá trị độ cứng thụt thu được bằng cách đo độ sâu hoặc các khu vực của sự thụt vào sử dụng một trong số hơn 12 phương pháp thử nghiệm khác nhau. Click vào đây để tìm hiểu thêm về vấn đề cơ bản kiểm tra độ cứng. Các phương pháp thử độ cứng Vickers, cũng được gọi là một phương pháp thử nghiệm microhardness, được sử dụng chủ yếu cho các bộ phận nhỏ, phần mỏng, hoặc làm việc hợp chiều sâu. Các phương pháp Vickers được dựa trên một hệ thống đo lường quang học. Các thủ tục kiểm tra Microhardness, ASTM E-384, xác định một loạt các tải trọng nhẹ sử dụng một indenter kim cương để làm xẹp được đo và chuyển đổi thành một giá trị độ cứng. Nó rất hữu ích để thử nghiệm trên một loại rộng của vật liệu miễn là mẫu thử nghiệm được chuẩn bị cẩn thận. Một hình vuông kim cương kim tự tháp hình cơ sở được sử dụng để thử nghiệm ở quy mô Vickers. Thông thường tải là rất nhẹ, dao động từ vài gam đến một hoặc một vài kg, mặc dù "vĩ mô" tải Vickers có thể lên tới 30 kg trở lên. . Các phương pháp Microhardness được sử dụng để thử nghiệm trên các kim loại, gốm sứ, vật liệu tổng hợp - gần như bất kỳ loại vật liệu từ các indentation thử nghiệm là rất nhỏ trong một thử nghiệm Vickers, nó rất hữu ích cho một loạt các ứng dụng: kiểm tra vật liệu rất mỏng như lá hoặc đo bề mặt của chi tiết, bộ phận nhỏ hoặc các khu vực nhỏ, đo vi cấu trúc cá nhân, hoặc đo độ sâu của trường hợp làm cứng bởi khi cắt một phần và thực hiện một loạt các vết lõm để mô tả một hồ sơ cá nhân của sự thay đổi độ cứng. Các phương pháp Vickers được sử dụng nhiều hơn. Chuẩn bị mẫu thường là cần thiết với một thử nghiệm microhardness để cung cấp một mẫu đủ nhỏ để có thể phù hợp với các tester. Ngoài ra, việc chuẩn bị mẫu sẽ cần phải làm cho bề mặt của mẫu vật mịn để cho phép một hình dạng thụt đầu dòng và thường xuyên đo lường tốt, và để đảm bảo mẫu có thể được tổ chức vuông góc với indenter. Thông thường các mẫu chuẩn bị được gắn trong một môi trường nhựa để thuận tiện cho việc chuẩn bị và thử nghiệm. Các vết lõm nên càng lớn càng tốt để tối đa hóa độ phân giải đo. (Lỗi được phóng đại như kích thước thụt giảm) Các thủ tục kiểm tra phụ thuộc vào vấn đề ảnh hưởng của điều hành trên các kết quả xét nghiệm.