The CeO2/RGA nanocomposites were ch

The CeO2/RGA nanocomposites were chemically synthesized using an ultrasonication assisted chemical method. In a typical synthetic process, 4 mg/mL of the above synthesized GO was added to 10 mL DI water and sonicated for 30 min to reduce the oxygen groups included in the GO. After that, 0.05 M of CeO2 nano- structures were dissolved in this solution, which was again sonicated for 30 min. 0.1 g vitamin-C was then added and uniformly mixed, and the suspension was vigorously sonicated for another
15 min to obtain a homogeneous suspension. Finally, the

suspension was left undisturbed and unstirred in a muffle furnace at 95 C for 8 h. The resultant hydrogels were first purified in a large volume of distilled water for at least a week in order to wash out low molecular weight components of the system, including excess vitamin-C and its oxidized product dehydroascorbic acid. Finally, the purified hydrogels were freeze-dried for 24 h to ensure complete removal of water molecules.

Kết quả (Việt) 2:

Các nanocomposites CeO2 / RGA được tổng hợp hóa học sử dụng một ultrasonication hỗ trợ phương pháp hóa học. Trong một quá trình tổng hợp điển hình, 4 mg / mL tổng hợp GO trên được thêm vào 10 ml nước DI và âm trong 30 phút để làm giảm các nhóm oxy có trong GO. Sau đó, 0,05 M của cấu trúc CeO2 nano được hòa tan trong dung dịch này, được một lần nữa âm trong 30 phút. 0,1 g vitamin C sau đó đã được bổ sung và thống nhất hỗn hợp, và hệ thống treo được mạnh mẽ âm trong một
15 phút để có được một hệ thống treo đồng nhất. Cuối cùng,

hệ thống treo đã bị xâm phạm và unstirred trong lò fl e MUF ở 95 C trong 8 h. Các hydrogel quả là fi đầu tiên puri fi ed trong một khối lượng lớn nước cất trong ít nhất một tuần để rửa ra thành phần trọng lượng phân tử thấp của hệ thống, bao gồm cả dư thừa vitamin C và sản phẩm oxy hóa axit dehydroascorbic của nó. Cuối cùng, ed hydrogel puri fi là đông khô trong 24 giờ để đảm bảo loại bỏ hoàn toàn các phân tử nước.