Study on Nd-Fe-B Sintered Permanent

Study on Nd-Fe-B Sintered Permanent Magnets Produced by Modifying Intergranular Phase

Study on Nd-Fe-B Sintered Permanent Magnets Produced by Modifying Intergranular Phase

Nd-Fe-B sintered magnets have been widely used in various applications due to their outstanding magnetic properties,and become the best important permanent magnets.However, poor corrosion resistance and low coercivity limit their applications and development.Both corrosion resistance and coercivity are very sensitive to intergranular phase.Therefore, modifying intergranular phase are very effective methods to improve both corrosion resistance and coercivity of Nd-Fe-B sintered magnets.In this dissertation,Nd-Fe-B sintered magnets were prepared by single alloy sintering method and binary alloy sintering method,respectively.Microstructure,corrosion resistance and coercivity of Nd-Fe-B sintered magnets NdFeB Permanent Magnets with intergranular addition of Cu60Zn40 and Mg70Zn30 powders were systematically investigated and analyzed,respectively.Meanwhile,the intergranular phase was modified by adding(Pr,Nd)32.5Fe62Cu5.5 alloy,and microstructure, corrosion resistance and coercivity of Nd-Fe-B sintered magnets were systematically investigated.The design principle of Nd-Fe-B sintered magnets with high corrosion resistance was suggested.The main results are as follows:Both corrosion resistance and magnetic properties of Nd-Fe-B sintered magnets are effectively improved with intergranular addition of Cu60Zn40 and Mg70Zn30 powders, respectively.Enhancement of the electrochemical potential of the intergranular phase,decrease of the total contents of Nd.uniform distribution of the Nd-rich phase and increase of magnet density are responsible for the corrosion resistance improvement.

Especially.the corrosion resistance of magnets with intergranular addition of Cu60Zn40 powders is improved approximately one order of magnitude in 3.5 wt%NaCl solution.Moreover,the uniform distribution of Nd-rich phase and grains refined resulting in the enhancement of coercivity,and the increase of magnet density leading to the improvement of remanence and maximum energy product.Modifying intergranular phase by adding(Pr,Nd)32.5Fe62Cu5.5 alloy can effectively improve corrosion resistance and coercivity of Nd-Fe-B sintered magnets.Corrosion current density of magnet with 12 wt%(Pr,Nd)32.5Fe62Cu5.5 alloy and RE30.2B0.96Febal magnets prepared by single alloy sintering method http://www.chinamagnets.biz are 3.484μA/cm2 and 9.870μA/cm2 in 3.5 wt%NaCl solution, respectively,exhibiting that the corrosion resistance of magnets with the addition of (Pr,Nd)32.5Fe62Cu5.5 alloy is effectively improved.Meanwhile,the enhancement of coercivity is about 69%in the case of 12 wt%(Pr,Nd)32.5Fe62Cu5.5 alloy addition compared with that for additive-free magnet.

Kết quả (Việt) 1:

Nghiên cứu các nam châm vĩnh cửu thiêu kết Nd-Fe-B được sản xuất bằng cách sửa đổi Intergranular giai đoạn Nghiên cứu các nam châm vĩnh cửu thiêu kết Nd-Fe-B được sản xuất bằng cách sửa đổi Intergranular giai đoạn Nd-Fe-B thiêu kết nam châm đã được rộng rãi được sử dụng trong các ứng dụng khác nhau do tính chất từ xuất sắc của họ, và trở thành các tốt nhất quan trọng thường trú nam châm. Tuy nhiên, chống ăn mòn nghèo và vật liệu từ mềm thấp giới hạn của ứng dụng và phát triển. Chống ăn mòn và vật liệu từ mềm là rất nhạy cảm với intergranular giai đoạn. Do đó, việc sửa đổi intergranular giai đoạn là các phương pháp rất hiệu quả để cải thiện khả năng chống ăn mòn và vật liệu từ mềm Nd-Fe-B thiêu kết nam châm. Trong luận án này, Nd-Fe-B thiêu kết nam châm đã được chuẩn bị bởi đơn hợp kim sintering phương pháp và hợp kim nhị phân máy phương pháp, tương ứng. Microstructure, chống ăn mòn và vật liệu từ mềm Nd-Fe-B thiêu kết nam châm NdFeB nam châm vĩnh cửu với intergranular bổ sung của Cu60Zn40 và Mg70Zn30 bột có hệ thống đã được điều tra và phân tích, tương ứng. Trong khi đó, giai đoạn intergranular đổi lần bằng cách thêm (Pr, Nd) hợp kim 32.5Fe62Cu5.5, và microstructure, chống ăn mòn và vật liệu từ mềm Nd-Fe-B thiêu kết nam châm có hệ thống đã được điều tra. Nguyên tắc thiết kế Nd-Fe-B thiêu kết nam châm với chống ăn mòn cao được đề nghị. Các kết quả chính là như sau: cả hai sự ăn mòn kháng và tính chất từ của Nd-Fe-B thiêu kết nam châm được hiệu quả cải thiện với intergranular bổ sung của bột Cu60Zn40 và Mg70Zn30, tương ứng. Nâng cao tiềm năng điện hóa của giai đoạn intergranular, giảm tất cả nội dung của Nd.uniform phân phối của giai đoạn Nd giàu và tăng mật độ nam châm chịu trách nhiệm cho việc cải thiện khả năng chống ăn mòn. Especially.the corrosion resistance of magnets with intergranular addition of Cu60Zn40 powders is improved approximately one order of magnitude in 3.5 wt%NaCl solution.Moreover,the uniform distribution of Nd-rich phase and grains refined resulting in the enhancement of coercivity,and the increase of magnet density leading to the improvement of remanence and maximum energy product.Modifying intergranular phase by adding(Pr,Nd)32.5Fe62Cu5.5 alloy can effectively improve corrosion resistance and coercivity of Nd-Fe-B sintered magnets.Corrosion current density of magnet with 12 wt%(Pr,Nd)32.5Fe62Cu5.5 alloy and RE30.2B0.96Febal magnets prepared by single alloy sintering method http://www.chinamagnets.biz are 3.484μA/cm2 and 9.870μA/cm2 in 3.5 wt%NaCl solution, respectively,exhibiting that the corrosion resistance of magnets with the addition of (Pr,Nd)32.5Fe62Cu5.5 alloy is effectively improved.Meanwhile,the enhancement of coercivity is about 69%in the case of 12 wt%(Pr,Nd)32.5Fe62Cu5.5 alloy addition compared with that for additive-free magnet.

Kết quả (Việt) 2:

Nghiên cứu về Nd-Fe-B thiêu kết Châm Vĩnh Cửu được sản xuất bởi Sửa đổi giữa các hạt pha Nghiên cứu Nd-Fe-B thiêu kết Châm Vĩnh Cửu được sản xuất bởi Sửa đổi giữa các hạt pha Nd-Fe-B nam châm thiêu kết đã được sử dụng rộng rãi trong các ứng dụng khác nhau do tính chất từ xuất sắc của họ , và trở thành magnets.However tốt nhất quan trọng lâu dài, chống ăn mòn nghèo và kháng từ thấp hạn chế các ứng dụng của họ và khả năng chống ăn mòn development.Both và kháng từ rất nhạy cảm với phase.Therefore giữa các hạt, sửa đổi giai đoạn giữa các hạt được phương pháp rất hiệu quả để cải thiện cả năng chống ăn mòn và kháng từ của Nd-Fe-B magnets.In thiêu kết luận án này, nam châm thiêu kết Nd-Fe-B đã được chuẩn bị bằng phương pháp đơn hợp kim thiêu kết và phương pháp hợp kim thiêu kết nhị phân, respectively.Microstructure, chống ăn mòn và kháng từ của nam châm thiêu kết Nd-Fe-B NdFeB Nam châm vĩnh cửu với Ngoài ra giữa các hạt của Cu60Zn40 và Mg70Zn30 bột đã được nghiên cứu một cách hệ thống và phân tích, respectively.Meanwhile, giai đoạn giữa các hạt đã được sửa đổi bằng cách thêm (Pr, Nd) 32.5Fe62Cu5.5 hợp kim, và vi cấu trúc, khả năng chống ăn mòn và kháng từ của Nd-Fe nam châm thiêu kết -B là hệ thống investigated.The nguyên tắc thiết kế của nam châm thiêu kết Nd-Fe-B với chống ăn mòn cao là suggested.The kết quả chính như sau: Cả hai chống ăn mòn và tính chất từ của nam châm thiêu kết Nd-Fe-B được cải thiện hiệu quả Ngoài ra giữa các hạt với các Cu60Zn40 và Mg70Zn30 bột, respectively.Enhancement về tiềm năng điện hóa của giai đoạn giữa các hạt, giảm tổng số nội dung của Nd.uniform phân phối của giai đoạn Nd-phong phú và tăng mật độ nam châm chịu trách nhiệm cho việc cải thiện khả năng chống ăn mòn. Especially.the chống ăn mòn của nam châm với Ngoài ra giữa các hạt bột Cu60Zn40 được cải thiện khoảng một thứ tự cường độ 3,5% khối lượng NaCl solution.Moreover, phân phối thống nhất của Nd giàu pha và ngũ cốc tinh chế kết quả trong việc tăng cường độ kháng, và sự gia tăng mật độ điện từ hàng đầu để cải thiện remanence và product.Modifying năng lượng giai đoạn giữa các hạt tối đa bằng cách thêm (Pr, Nd) 32.5Fe62Cu5.5 hợp kim có thể cải thiện khả năng chống ăn mòn và kháng từ của Nd-Fe-B magnets.Corrosion thiêu kết mật độ hiện tại của nam châm với 12% khối lượng (Pr, Nd) 32.5Fe62Cu5.5 hợp kim và châm RE30.2B0.96Febal chuẩn bị bằng hợp kim duy nhất phương pháp thiêu kết http://www.chinamagnets.biz là 3.484μA / cm2 và 9.870μA / cm2 trong 3,5 wt% dung dịch NaCl, tương ứng, tham gia triển lãm là chống ăn mòn của nam châm với việc bổ sung (Pr, Nd) 32.5Fe62Cu5.5 hợp kim được hiệu quả improved.Meanwhile, việc tăng cường kháng từ khoảng 69% trong trường hợp của 12% khối lượng (Pr, Nd) 32.5Fe62Cu5.5 hợp kim Ngoài ra nhất so với nam châm phụ phí.