ExperimentalCharacterization method

Experimental
Characterization methods
Fourier Transform Infrared (FT-IR) spectra were recorded in the 400–4,000 cm
-1
spectral region based on a Perkin-Elmer FTIR paragon 1000 PC spectrometer by
dispersing the materials in KBr discs. UV–visible reflectance spectra were obtained
at room temperature by means of a Perkin-Elmer Lamda 8 spectrometer using
BaSO4 as reference. Elemental analysis (C, H, N) of organic compounds were
carried out on a Perkin-Elmer analyzer. Vanadium loading was measured by atomic
absorption spectrometry on a Perkin-Elmer 3100 apparatus, after sample dissolution
through acid attack. BET surface area was determined using N2 sorption data
measured at 77 K by means of a Micrometrics ASAP 2000 apparatus. The pore
diameter of the samples was determined from the desorption branch of N2
adsorption isotherm using the BJH method.

Kết quả (Việt) 1:

Thử nghiệmPhương pháp đặc tínhQuang phổ Fourier Transform hồng ngoại (FT-IR) được ghi nhận trong 400-4.000 cm-1quang phổ vùng dựa trên một paragon Perkin-Elmer FTIR 1000 PC phổ kế bởiphân tán các vật liệu trong KBr đĩa. Quang phổ UV-có thể nhìn thấy phản xạ đã thu đượcở nhiệt độ phòng bằng phương tiện của một sử dụng phổ kế Perkin-Elmer Lamda 8BaSO4 là tài liệu tham khảo. Phân tích nguyên tố (C, H, N) của hợp chất hữu cơ đãthực hiện trong một phân tích Perkin-Elmer. Vanadi tải được đo bằng nguyên tửhấp thụ spectrometry trên một bộ máy Perkin-Elmer 3100, sau khi mẫu tan rãthông qua axit tấn công. Diện tích bề mặt đặt cược đã được xác định bằng cách sử dụng N2 sorption dữ liệuđo tại 77 K bằng phương tiện của một bộ máy Micrometrics càng sớm càng tốt năm 2000. Lỗ chân lôngđường kính của các mẫu đã được xác định từ chi nhánh desorption của N2Hấp phụ isotherm bằng cách sử dụng phương pháp BJH.