Mechanical alloying was used in ord

Mechanical alloying was used in order to synthesize nanocrystallized ZnSb powder. It has been shown that after 3 h of milling and with an excess of zinc in the mixture of Zn + Sb powder, the ZnSb phase was obtained with crystallites size of 40 nm. This powder was characterized by X-ray diffraction using Rietveld refinement and differential thermal analysis before being sintered by Spark Plasma Sintering. We also present thermoelectric properties of ZnSb and a comparison is made with a solidified ingot of ZnSb. Thanks to our method of synthesis, the electrical properties (power factor) of ZnSb are stable in the temperatures range (300–700 K) and very close to the ones of Zn4Sb3which is the best thermoelectric material so far in the Zn–Sb system.

2016 Elsevier B.V. All rights reserved

Kết quả (Việt) 1:

Tạo hợp kim cơ khí được sử dụng để tổng hợp nanocrystallized ZnSb bột. Nó đã cho thấy rằng sau 3 h phay và với sự dư thừa kẽm trong hỗn hợp Zn + Sb bột, giai đoạn ZnSb đã thu được với crystallites kích thước 40 nm. Bột này được đặc trưng bởi nhiễu xạ tia x sử dụng Rietveld sàng lọc và phân tích nhiệt vi sai trước khi bị thiêu kết bằng tia Plasma Sintering. Chúng tôi cũng trình bày các tính chất điện của ZnSb và so sánh được thực hiện với một phôi kiên cố hóa của ZnSb. nhờ chúng tôi phương pháp tổng hợp, tính chất điện (power factor) ZnSb ổn định trong phạm vi nhiệt độ (300-700 K) và rất gần với những người thân của Zn4Sb3which là các vật liệu điện tốt nhất cho đến nay trong hệ thống Zn-Sb.2016 Elsevier B.V Tất cả các quyền