Figure 4A shows plates to which a 1

Figure 4A shows plates to which a 100-l bacterial suspension
(approximately 107 CFU/ml) was applied. The presence of
nanoparticles at a certain level inhibited bacterial growth by
more than 90%. Interestingly, however, this level is signifi-
cantly different for different nanoparticle shapes. For truncated
triangular particles, almost complete inhibition of bacterial
growth was observed even at a total silver content of 1
g. In the case of spherical nanoparticles, a total silver content
above 12.5 g reduced the number of colonies significantly,
while a total of 50 to 100 g of silver caused 100% inhibition
of bacterial growth. Rod-shaped nanoparticles and AgNO3
showed inferior performance. Even in the presence of 100 g
of rod-shaped particles, some colonies grew on the plate,
though fewer than with an identical AgNO3 dose.

Kết quả (Việt) 2:

Hình 4A cho thấy tấm mà một 100-? L đình chỉ do vi khuẩn
(khoảng 107 CFU / ml) đã được áp dụng. Sự có mặt của
các hạt nano ở một mức độ nào đó ức chế vi khuẩn phát triển bởi
hơn 90%. Thật thú vị, tuy nhiên, mức này là kể
đáng khác nhau cho các hình dạng hạt nano khác nhau. Đối với cắt ngắn
các hạt hình tam giác, ức chế gần như hoàn toàn vi khuẩn
tăng trưởng đã được quan sát thấy ngay cả ở một số nội dung bạc của 1
g?. Trong trường hợp của các hạt nano hình cầu, tổng hàm lượng bạc
trên 12,5? G giảm số lượng các thuộc địa đáng kể,
trong khi tổng số 50-100? G bạc gây ra 100% ức chế
vi khuẩn phát triển. Hình que hạt nano và AgNO3
cho thấy hiệu suất kém hơn. Ngay cả trong sự hiện diện của 100? G
của các hạt hình que, một số khuẩn lạc mọc trên đĩa,
mặc dù ít hơn so với một liều lượng AgNO3 giống hệt nhau.