1. ASSIENMENT [2] METAL FORMING REV

1. ASSIENMENT [2] METAL FORMING REVIEW QUESTIONS1- What are the differences between bulk deformation processes and sheet metal processes?Answer. In bulk deformation, the shape changes are significant, and the work parts have alow area-to-volume ratio. In sheet metal processes, the area-to-volume ratio is high.2- Extrusion is a fundamental shaping process. Describe it. Answer. Extrusion is a compression process in which the work material is forced to flow through a die orifice, thereby forcing its cross section to assume the profile of the orifice.3- Why is the term press working often used for sheet metal processes? Answer. The term press working is used because most sheet metal operations are performed on presses.4- What is the difference between deep drawing and bar drawing? Answer. Deep drawing is a sheet metal forming process used to fabricate cup-shaped parts; bar drawing is a bulk deformation process used to reduce the diameter of a cylindrical work part.5- Indicate the mathematical equation for the flow curve. Answer. The flow curve is defined in Eq. (18.1) as Yf = Kεn.6- List some of the products produced on a rolling mill. Answer. Rolled products include flatsheet and plate stock, round bar and rod stock, rails, structural shapes such as I-beams andchannels.7- What is draft in a rolling operation? Answer. Draft is the difference between the starting thickness and the final thickness as the workpiece passes between the two opposing rolls.8- What is sticking in a hot rolling operation? Answer. Sticking is a condition in hot rolling in which the surface of the workpiece adheres to the rolls as the piece passes between the rolls, causing severe deformation of the metal below the surface in order to allow passage through the roll gap.9- Identify some of the ways in which force in flat rolling can be reduced. Answer. Ways to reduce force in flat rolling include (1) use hot rolling, (2) reduce draft in each pass, and (3) use smaller diameter rolls. 19.19 Distinguish between direct and indirect extrusion. Answer. In direct extrusion, also known as forward extrusion, a metal billet is loaded into a container, and a ram compresses the material, forcing it to flow through a die opening at the opposite end of the container. In indirect extrusion, also known as backward extrusion, the die is incorporated into the ram, and as the ram compresses into the metal billet, the metal is forced to flow through the die opening in a direction that is opposite (backwards) of the ram motion.10- Name some products that are produced by extrusion.
2. Answer. Products produced by continuous extrusion include structural shapes (window frames, shower stalls, channels), tubes and pipes, and rods of various cross sections. Products made by discrete extrusion include toothpaste tubes, aluminium beverage cans, and battery cases.11- In blanking of a circular sheet metal part, is the clearance applied to the punch diameter orthe die diameter? Answer. The die diameter equals the blank diameter, and the punch diameter is smaller by twice the clearance. Multiple Choice QUESTIONS 1- Which of the following is typical of the starting work geometry in sheet metal processes: (a) high volume-to-area ratio or (b) low volume-to-area ratio? Answer. (b).2- The flow curve expresses the behaviour of a metal in which of the following regions of the stress-strain curve: (a) elastic region or (b) plastic region? Answer. (b).3- The average flow stress is the flow stress multiplied by which of the following factors: (a) n, (b) (1+n), (c) 1/n, or (d) 1/(1+n), where n is the strain hardening exponent? Answer. (d).4- Hot working of metals refers to which one of the following temperature regions relative to the melting point of the given metal on an absolute temperature scale: (a) room temperature, (b) 0.2Tm, (c) 0.4Tm, or (d) 0.6Tm? Answer. (d).5- The starting workpiece in steel hot rolling of plate and sheet stock is which of the following(one best answer): (a) bar stock, (b) billet, (c) bloom, (d) slab, or (e) wire stock? Answer. (d).6- The maximum possible draft in a rolling operation depends on which of the following parameters (two correct answers): (a) coefficient of friction between roll and work, (b) roll diameter, (c) roll velocity, (d) stock thickness, (e) strain, and (f) strength coefficient of the work metal? Answer. (a) and (b).7- Which of the following are alternative names for indirect extrusion (two correct answers):(a) backward extrusion, (b) direct extrusion, (c) forward extrusion, (d) impact extrusion, and(e) reverse extrusion?Answer. (a) and (e).8- The production of tubing is possible in indirect extrusion but not in direct extrusion: (a) true or (b) false?
3. Answer. (b). Tube and pipe cross sections can be produced by either direct or indirectextrusion.9- Which of the following stress or strength parameters is used in the computation of the force in an extrusion operation (one best answer): (a) average flow stress, (b) compression strength, (c) final flow stress, (d) tensile strength, (e) yield strength? Answer. (a).10- In which of the following extrusion operation is friction a factor in determining theextrusion force (one best answer): (a) direct extrusion or (b) indirect extrusion? Answer. (a).11- A circular sheet metal slug produced in a hole punching operation will have the samediameter as which of the following: (a) the die opening or (b) the punch?Answer. (a).12- The cutting force in a sheet metal blanking operation depends on which mechanicalproperty of the metal (one correct answer): (a) compressive strength, (b) modulus of elasticity,(c) shear strength, (d) strain rate, (e) tensile strength, or (f) yield strength?Answer. (c).13- The holding force in drawing is most likely to be (a) greater than, (b) equal to, or (c) lessthan the maximum drawing force?Answer. (c). PROBLEMS1- The strength coefficient = 550 MPa and strain-hardening exponent = 0.22 for a certainmetal. During a forming operation, the final true strain that the metal experiences = 0.85.Determine the flow stress at this strain and the average flow stress that the metal experiencedduring the operation. Solution: Flow stress Yf = 550(0.85)0.22 = 531 MPa. Average flow stress fY= 550(0.85)0.22/1.22 = 435 MPa. 2- A metal has a flow curve with parameters: strength coefficient = 850 MPa and strain-hardening exponent = 0.30. A tensile specimen of the metal with gage length = 100 mm isstretched to a length = 157 mm. Determine the flow stress at the new length and the averageflow stress that the metal has been subjected to during the deformation. Solution: ε = ln (157/100) = ln 1.57 = 0.451 Flow stress Yf = 850(0.451)0.30 = 669.4 MPa. Average flow stress fY= 850(0.451)0.30/1.30 = 514.9 MPa.3- For a certain metal, the strength coefficient = 700 MPa and strain-hardening exponent= 0.27. Determine the average flow stress that the metal experiences if it is subjected to astress that is equal to its strength coefficient K. Solution: Yf = K = 700 = Kεn = 700ε.27 ε must be equal to 1.0.
4. fY= 700(1.0).27/1.27 = 700/1.27 = 551.2 MPa4- Determine the value of the strain-hardening exponent for a metal that will cause theaverage flow stress to be 3/4 of the final flow stress after deformation. Solution: fY= 0.75 Yf Kεn/(1+n) = 0.75 Kεn 1/(1+n) = 0.75 1 = 0.75(1+n) = 0.75 + 0.75n 0.25 = 0.75n n = 0.3335- A 2.0 in thick slab is 10.0 in wide and 12.0 ft long. Thickness is to be reduced in threesteps in a hot rolling operation. Each step will reduce the slab to 75% of its previousthickness. It is expected that for this metal and reduction, the slab will widen by 3% in eachstep. If the entry speed of the slab in the first step is 40 ft/min, and roll speed is the same forthe three steps, determine: (a) length and (b) exit velocity of the slab after the final reduction. Solution: (a) After three passes, tf = (0.75)(0.75)(0.75)(2.0) = 0.844 in wf = (1.03)(1.03)(1.03)(10.0) = 10.927 in towoLo = tfwfLf (2.0)(10.0)(12 x 12) = (0.844)(10.927)Lf Lf = (2.0)(10.0)(12 x 12)/(0.844)(10.927) = 312.3 in = 26.025 ft (b) Given that roll speed is the same at all three stands and that towovo = tfwfvf ,6- Determine the blanking force required in Problem 20.2, if the steel has shear strength = 325MPa and the tensile strength is 450 MPa. Solution: F = StL t = 2.0 mm from Problem 20.2. L = πD = 75π = 235.65 mm F = 325(2.0)(235.65) = 153,200 N7- Determine the tonnage requirement for the blanking operation in Problem 20.4, given thatthe stainless steel has a shear strength = 600 MPa. Solution: F = StL t = 4 mm from Problem 20.4. L = 85 + 50 + 25 + 25 + 35 + 25 + 25 + 50 = 320 mm F = 600(4.0)(320) = 768,000 N. This is abou

Kết quả (Việt) 1:

1. ASSIENMENT [2] kim loại hình thành REVIEW QUESTIONS1 - sự khác biệt giữa số lượng lớn các quá trình biến dạng và tấm kim loại quá trình? Câu trả lời. Trong biến dạng số lượng lớn, thay đổi hình dạng là rất lớn, và các bộ phận làm việc có alow tích khối lượng tỷ lệ. Trong quá trình kim loại tấm, thị trấn này có tỷ lệ tích khối lượng là high.2-đùn là một quá trình hình thành cơ bản. Mô tả nó. Câu trả lời. Phun ra là một quá trình nén trong đó tài liệu làm việc phải chảy qua một lỗ chết, do đó buộc của nó cắt ngang để thừa nhận hồ sơ của orifice.3-tại sao được báo chí hạn làm việc thường xuyên được sử dụng cho các tấm kim loại quy trình? Câu trả lời. Thuật ngữ báo chí làm việc được sử dụng bởi vì hầu hết tấm kim loại hoạt động được thực hiện trên presses.4-những gì là sự khác biệt giữa sâu vẽ và bar vẽ? Câu trả lời. Sâu vẽ là một tấm kim loại hình thành quá trình sử dụng để chế tạo các bộ phận hình chén; Bar vẽ là một quá trình biến dạng số lượng lớn được sử dụng để làm giảm đường kính của một tác phẩm hình trụ part.5-chỉ phương trình toán học cho các đường cong lưu lượng. Câu trả lời. Đường cong lưu lượng được định nghĩa trong Eq. (18.1) là Yf = Kεn.6 - danh sách một số các sản phẩm sản xuất trên một cán. Câu trả lời. Sản phẩm cán bao gồm flatsheet và tấm cổ, vòng bar và cây gậy cổ, Lan can, kết cấu hình dạng như tôi-dầm andchannels.7-những gì là dự thảo một hoạt động lăn? Câu trả lời. Dự thảo là sự khác biệt giữa độ dày khởi đầu và cuối cùng độ dày các phôi đã vượt qua giữa hai đối diện rolls.8-những gì gắn bó trong một hoạt động cán nóng? Câu trả lời. Gắn bó là một điều kiện trong cán nóng trong đó bề mặt của các phôi tuân thủ các cuộn các mảnh đã vượt qua giữa các cuộn, gây ra các biến dạng nghiêm trọng của kim loại dưới mặt đất để cho phép đi qua các cuộn gap.9-xác định một số trong những cách mà trong đó các lực lượng trong phẳng cán có thể được giảm. Câu trả lời. Cách để giảm lực lượng cán bằng phẳng bao gồm (1) sử dụng nóng cán, (2) giảm dự thảo ở mỗi pass, và đường kính nhỏ hơn (3) sử dụng cuộn. 19.19 phân biệt giữa phun ra trực tiếp và gián tiếp. Câu trả lời. Trong phun ra trực tiếp, cũng được gọi là phun ra phía trước, một phôi thép kim loại được nạp vào một thùng chứa, và một bộ nhớ ram nén các tài liệu, buộc nó để chảy qua một chết mở phía đối diện của container. Trong phun ra gián tiếp, còn được gọi là lạc hậu đùn, chết được tích hợp vào bộ nhớ ram, và như ram nén thành phôi thép kim loại, kim loại buộc phải chảy qua chết mở trong một hướng đó là đối diện (ngược) của ram motion.10-tên một số sản phẩm được sản xuất bởi phun ra.2. Answer. Products produced by continuous extrusion include structural shapes (window frames, shower stalls, channels), tubes and pipes, and rods of various cross sections. Products made by discrete extrusion include toothpaste tubes, aluminium beverage cans, and battery cases.11- In blanking of a circular sheet metal part, is the clearance applied to the punch diameter orthe die diameter? Answer. The die diameter equals the blank diameter, and the punch diameter is smaller by twice the clearance. Multiple Choice QUESTIONS 1- Which of the following is typical of the starting work geometry in sheet metal processes: (a) high volume-to-area ratio or (b) low volume-to-area ratio? Answer. (b).2- The flow curve expresses the behaviour of a metal in which of the following regions of the stress-strain curve: (a) elastic region or (b) plastic region? Answer. (b).3- The average flow stress is the flow stress multiplied by which of the following factors: (a) n, (b) (1+n), (c) 1/n, or (d) 1/(1+n), where n is the strain hardening exponent? Answer. (d).4- Hot working of metals refers to which one of the following temperature regions relative to the melting point of the given metal on an absolute temperature scale: (a) room temperature, (b) 0.2Tm, (c) 0.4Tm, or (d) 0.6Tm? Answer. (d).5- The starting workpiece in steel hot rolling of plate and sheet stock is which of the following(one best answer): (a) bar stock, (b) billet, (c) bloom, (d) slab, or (e) wire stock? Answer. (d).6- The maximum possible draft in a rolling operation depends on which of the following parameters (two correct answers): (a) coefficient of friction between roll and work, (b) roll diameter, (c) roll velocity, (d) stock thickness, (e) strain, and (f) strength coefficient of the work metal? Answer. (a) and (b).7- Which of the following are alternative names for indirect extrusion (two correct answers):(a) backward extrusion, (b) direct extrusion, (c) forward extrusion, (d) impact extrusion, and(e) reverse extrusion?Answer. (a) and (e).8- The production of tubing is possible in indirect extrusion but not in direct extrusion: (a) true or (b) false?3. Answer. (b). Tube and pipe cross sections can be produced by either direct or indirectextrusion.9- Which of the following stress or strength parameters is used in the computation of the force in an extrusion operation (one best answer): (a) average flow stress, (b) compression strength, (c) final flow stress, (d) tensile strength, (e) yield strength? Answer. (a).10- In which of the following extrusion operation is friction a factor in determining theextrusion force (one best answer): (a) direct extrusion or (b) indirect extrusion? Answer. (a).11- A circular sheet metal slug produced in a hole punching operation will have the samediameter as which of the following: (a) the die opening or (b) the punch?Answer. (a).12- The cutting force in a sheet metal blanking operation depends on which mechanicalproperty of the metal (one correct answer): (a) compressive strength, (b) modulus of elasticity,(c) shear strength, (d) strain rate, (e) tensile strength, or (f) yield strength?Answer. (c).13- The holding force in drawing is most likely to be (a) greater than, (b) equal to, or (c) lessthan the maximum drawing force?Answer. (c). PROBLEMS1- The strength coefficient = 550 MPa and strain-hardening exponent = 0.22 for a certainmetal. During a forming operation, the final true strain that the metal experiences = 0.85.Determine the flow stress at this strain and the average flow stress that the metal experiencedduring the operation. Solution: Flow stress Yf = 550(0.85)0.22 = 531 MPa. Average flow stress fY= 550(0.85)0.22/1.22 = 435 MPa. 2- A metal has a flow curve with parameters: strength coefficient = 850 MPa and strain-hardening exponent = 0.30. A tensile specimen of the metal with gage length = 100 mm isstretched to a length = 157 mm. Determine the flow stress at the new length and the averageflow stress that the metal has been subjected to during the deformation. Solution: ε = ln (157/100) = ln 1.57 = 0.451 Flow stress Yf = 850(0.451)0.30 = 669.4 MPa. Average flow stress fY= 850(0.451)0.30/1.30 = 514.9 MPa.3- For a certain metal, the strength coefficient = 700 MPa and strain-hardening exponent= 0.27. Determine the average flow stress that the metal experiences if it is subjected to astress that is equal to its strength coefficient K. Solution: Yf = K = 700 = Kεn = 700ε.27 ε must be equal to 1.0.4. fY= 700(1.0).27/1.27 = 700/1.27 = 551.2 MPa4- Determine the value of the strain-hardening exponent for a metal that will cause theaverage flow stress to be 3/4 of the final flow stress after deformation. Solution: fY= 0.75 Yf Kεn/(1+n) = 0.75 Kεn 1/(1+n) = 0.75 1 = 0.75(1+n) = 0.75 + 0.75n 0.25 = 0.75n n = 0.3335- A 2.0 in thick slab is 10.0 in wide and 12.0 ft long. Thickness is to be reduced in threesteps in a hot rolling operation. Each step will reduce the slab to 75% of its previousthickness. It is expected that for this metal and reduction, the slab will widen by 3% in eachstep. If the entry speed of the slab in the first step is 40 ft/min, and roll speed is the same forthe three steps, determine: (a) length and (b) exit velocity of the slab after the final reduction. Solution: (a) After three passes, tf = (0.75)(0.75)(0.75)(2.0) = 0.844 in wf = (1.03)(1.03)(1.03)(10.0) = 10.927 in towoLo = tfwfLf (2.0)(10.0)(12 x 12) = (0.844)(10.927)Lf Lf = (2.0)(10.0)(12 x 12)/(0.844)(10.927) = 312.3 in = 26.025 ft (b) Given that roll speed is the same at all three stands and that towovo = tfwfvf ,6- Determine the blanking force required in Problem 20.2, if the steel has shear strength = 325MPa and the tensile strength is 450 MPa. Solution: F = StL t = 2.0 mm from Problem 20.2. L = πD = 75π = 235.65 mm F = 325(2.0)(235.65) = 153,200 N7- Determine the tonnage requirement for the blanking operation in Problem 20.4, given thatthe stainless steel has a shear strength = 600 MPa. Solution: F = StL t = 4 mm from Problem 20.4. L = 85 + 50 + 25 + 25 + 35 + 25 + 25 + 50 = 320 mm F = 600(4.0)(320) = 768,000 N. This is abou

Kết quả (Việt) 2:

1. ASSIENMENT [2] METAL HÌNH THÀNH TỔNG QUESTIONS1- sự khác biệt giữa các quá trình biến dạng lớn và quá trình kim loại tấm là gì? Trả lời. Trong biến dạng rời, thay đổi hình dạng là đáng kể, và các bộ phận công trình có tỷ lệ diện tích alow-to-khối lượng. Trong quá trình kim loại tấm, tỷ lệ diện tích-to-khối lượng là đùn high.2- là một quá trình định hình cơ bản. Miêu tả nó. Bài giải. Đùn là một quá trình nén trong đó vật liệu công việc buộc phải chảy qua một lỗ chết, do đó buộc cắt ngang của nó để giả hồ sơ cá nhân của orifice.3- Tại sao báo chí hạn bộ làm việc thường được sử dụng cho quá trình kim loại tấm? Bài giải. Các hoạt động báo chí hạn được sử dụng bởi vì các hoạt động kim loại nhất tấm được thực hiện trên presses.4- sự khác biệt giữa bản vẽ sâu và thanh vẽ là gì? Bài giải. Sâu vẽ là một tấm kim loại hình thành quá trình sử dụng để chế tạo các bộ phận hình chén; thanh vẽ là một quá trình biến dạng với số lượng lớn được sử dụng để làm giảm đường kính của một tác phẩm hình trụ part.5- Chỉ ra phương trình toán học cho các đường cong dòng chảy. Bài giải. Các đường cong dòng chảy được xác định trong phương trình. (18.1) là YF = Kεn.6- Danh sách một số các sản phẩm được sản xuất trên một dây chuyền cán. Bài giải. Sản phẩm bao gồm cán flatsheet và chứng khoán tấm, thanh tròn và cổ phiếu thanh, đường ray, hình dạng cấu trúc như I-dầm andchannels.7- dự thảo trong một hoạt động lăn là gì? Bài giải. Dự thảo là sự khác biệt giữa độ dày bắt đầu và độ dày cuối cùng như các phôi đi qua giữa hai đối rolls.8- gì là gắn bó trong một hoạt động cán nóng? Bài giải. Gắn bó là tình trạng cán nóng trong đó bề mặt của phôi tuân thủ các cuộn như những mảnh chuyển giữa các cuộn, gây biến dạng nghiêm trọng của kim loại bên dưới bề mặt để cho phép đi qua các cuộn gap.9- Xác định một số những cách thức mà lực lượng trong cán phẳng có thể được giảm bớt. Bài giải. Cách để giảm lực trong cán phẳng bao gồm (1) sử dụng cán nóng, (2) giảm dự thảo trong từng vượt qua, và (3) sử dụng cuộn đường kính nhỏ hơn. 19,19 Phân biệt giữa đùn trực tiếp và gián tiếp. Bài giải. Trong đùn trực tiếp, còn được gọi là phía trước phun ra, một phôi kim loại được nạp vào một container, và một ram nén vật liệu, buộc phải chảy qua một lỗ chết ở cuối đối diện của hộp đựng. Trong đùn gián tiếp, còn được gọi là đùn lạc hậu, sự chết đã được đưa vào ram, và như ram nén vào phôi kim loại, kim loại được ép chảy qua lỗ chết theo một hướng mà là ngược lại (lùi) của ram motion.10- Tên một số sản phẩm được sản xuất bằng cách phun ra.
2. Bài giải. Sản phẩm được sản xuất bằng cách đùn liên tục bao gồm hình dạng cấu trúc (các khung cửa sổ, quầy hàng hoa sen, kênh), ống và ống dẫn, và que mặt cắt khác nhau. Sản phẩm làm bằng đùn rời rạc bao gồm ống kem đánh răng, lon nhôm nước giải khát, và cases.11- pin Trong tẩy trống của một phần kim loại tấm tròn, được giải phóng mặt bằng áp dụng cho các đường kính đấm orthe chết đường kính? Bài giải. Đường kính đế bằng với đường kính trống, và đường kính đục lỗ nhỏ bằng hai lần giải phóng mặt bằng. Nhiều sự lựa chọn câu hỏi 1- Điều nào sau đây là điển hình của hình học bắt đầu công việc trong quá trình kim loại tấm: (a) Tỷ lệ khối lượng cao-to-khu vực hoặc (b) tỷ lệ thấp khối lượng-to-khu vực? Bài giải. (b) .2- Các đường cong dòng chảy thể hiện hành vi của một kim loại trong đó các vùng sau của đường cong ứng suất biến dạng: (a) khu vực đàn hồi hoặc (b) khu vực nhựa? Bài giải. (b) .3- Sự căng thẳng dòng chảy trung bình là sự căng thẳng dòng chảy nhân mà trong những yếu tố sau đây: (a) n, (b) (1 + n), (c) 1 / n, hoặc (d) 1 / ( 1 + n), trong đó n là số mũ căng cứng? Bài giải. (d) .4- làm việc nóng của kim loại dùng để chỉ mà một trong những vùng nhiệt độ sau đây tương ứng với điểm nóng chảy của kim loại nhất định trên một thang đo nhiệt độ tuyệt đối: (a) nhiệt độ phòng, (b) 0.2Tm, (c) 0.4 Tm, hoặc (d) 0.6Tm? Bài giải. (d) .5- Phôi bắt đầu từ thép cán nóng thép tấm và chứng khoán là tấm đó của (một câu trả lời tốt nhất) sau đây: (a) cổ phiếu thanh, (b) phôi thép, (c) nở, (d) phiến, hoặc (e) cổ dây? Bài giải. (d) .6- Dự thảo tối đa có thể trong một hoạt động lăn phụ thuộc vào các thông số sau (hai câu trả lời đúng): (a) hệ số ma sát giữa cuộn và làm việc, (b) đường kính cuộn, (c) vận tốc roll, (d) độ dày cổ phiếu, (e) căng thẳng, và (f) Hệ số sức mạnh của kim loại công việc? Bài giải. (a) và (b) .7- Điều nào sau đây là những cái tên thay thế cho đùn gián tiếp (hai câu trả lời đúng) :( a) đùn lạc hậu, (b) đùn trực tiếp, (c) về phía trước phun ra, (d) tác động đùn, và (e) đùn ngược? trả lời. (a) và (e) .8- Việc sản xuất của ống có thể đùn gián tiếp nhưng không đùn trực tiếp: (a) đúng hoặc (b) sai?
3. Bài giải. (b). Phần ống và ống chéo có thể được sản xuất bằng cách trực tiếp hoặc indirectextrusion.9- Mà các thông số căng thẳng hoặc sức mạnh sau đây được sử dụng trong tính toán của các lực lượng trong một hoạt động đùn (một câu trả lời tốt nhất): (a) căng thẳng dòng chảy trung bình, ( b) Cường độ nén, (c) stress dòng cuối cùng, (d) độ bền kéo, (e) mang lại sức mạnh? Bài giải. (a) .10- Trong đó các hoạt động sau đây là đùn ma sát là một yếu tố trong việc xác định lực lượng theextrusion (một câu trả lời tốt nhất): (a) đùn trực tiếp hoặc (b) đùn gián tiếp? Bài giải. (a) .11- Sên tấm kim loại hình tròn được sản xuất trong một hoạt động lỗ đấm sẽ có samediameter như nào sau đây: (a) khai mạc chết hoặc (b) những cú đấm trả lời. (a) .12- Lực cắt trong một hoạt động kim loại tấm tẩy trống tùy thuộc vào mechanicalproperty của kim loại (một câu trả lời đúng): (a) cường độ nén, (b) mô đun đàn hồi, (c) sức chống cắt, (d) Tỷ lệ biến dạng, (e) độ bền kéo, hoặc (f) mang lại sức mạnh? trả lời. (c) .13- Lực lượng nắm giữ trong bản vẽ là nhiều khả năng là (a) lớn hơn, (b) bằng hoặc (c) lessthan lực lượng bản vẽ tối đa? trả lời. (c). PROBLEMS1- Hệ số sức mạnh = 550 MPa và căng thẳng-cứng mũ = 0.22 cho một certainmetal. Trong một hoạt động tạo hình, căng thẳng thật sự cuối cùng mà những kinh nghiệm kim loại = 0.85.Determine sự căng thẳng dòng chảy ở dòng này và sự căng thẳng dòng chảy trung bình mà các kim loại experiencedduring hoạt động. Giải pháp: Flow căng thẳng YF = 550 (0,85) 0,22 = 531 MPa. Căng thẳng dòng chảy trung bình fy = 550 (0,85) 0,22 / 1,22 = 435 MPa. 2- Một kim loại có một đường cong dòng chảy với các thông số: hệ số sức mạnh = 850 MPa và căng thẳng-cứng mũ = 0,30. Một mẫu vật kéo của kim loại với chiều dài gage = 100 mm isstretched đến một chiều dài = 157 mm. Xác định căng thẳng dòng chảy ở chiều dài mới và sự căng thẳng averageflow rằng các kim loại đã phải chịu trong quá trình biến dạng. Giải pháp: ε = ln (157/100) = ln 1,57 = 0,451 Dòng nhấn mạnh YF = 850 (0,451) 0,30 = 669,4 MPa. Trung bình căng thẳng dòng chảy fy = 850 (0,451) 0,30 / 1,30 = 514,9 MPa.3- Đối với một kim loại nhất định, hệ số sức mạnh = 700 MPa và căng thẳng-cứng mũ = 0,27. Xác định căng thẳng dòng chảy trung bình mà các kinh nghiệm kim loại nếu nó chịu astress đó là bằng với hệ số sức mạnh của nó K. Giải pháp:. YF = K = 700 = Kεn = 700ε.27 ε phải bằng 1,0
4. fy = 700 (1.0) 0,27 / 1,27 = 700 / 1,27 = 551,2 MPa4- Xác định giá trị của các số mũ căng-cứng cho một kim loại mà sẽ gây ra căng thẳng dòng chảy theaverage là 3/4 của sự căng thẳng dòng cuối cùng sau khi biến dạng. Giải pháp: fy = 0,75 YF Kεn / (1 ​​+ n) = 0,75 Kεn 1 / (1 ​​+ n) = 0,75 1 = 0.75 (1 + n) = 0,75 + 0,25 = 0.75n 0.75nn = 0.3335- A 2.0 trong tấm dày là 10,0 trong rộng và dài 12,0 ft. Độ dày được giảm xuống trong threesteps trong một hoạt động cán nóng. Mỗi bước sẽ làm giảm sàn 75% previousthickness của nó. Dự kiến đối với kim loại này giảm, các sàn sẽ phình thêm 3% trong eachstep. Nếu tốc độ xâm nhập của các phiến trong bước đầu tiên là 40 ft / min, và tốc độ cuộn là giống forthe ba bước, xác định: (a) chiều dài và (b) vận tốc thoát của phiến sau khi giảm thức. Giải pháp: (a) Sau khi ba đi, tf = (0,75) (0,75) (0,75) (2,0) = 0,844 trong wf = (1.03) (1.03) (1.03) (10,0) = 10,927 trong towoLo = tfwfLf (2.0) ( 10.0) (12 x 12) = (0,844) (10,927) Lf Lf = (2,0) (10,0) (12 x 12) / (0,844) (10,927) = 312,3 in = 26,025 ft (b) Cho rằng cuộn tốc độ là cùng một lúc cả ba khán đài và rằng towovo = tfwfvf, 6- Xác định lực tẩy trống cần thiết trong vấn đề 20.2, nếu thép có cường độ chịu cắt = 325MPa và độ bền kéo là 450 MPa. Giải pháp: F = STL t = 2,0 mm từ Problem 20.2. L = πD = 75π = 235,65 mm F = 325 (2.0) (235,65) = 153.200 N7- Xác định các yêu cầu trọng tải cho các hoạt động tẩy trống trong bài tập 20.4, trao thatthe thép không gỉ có độ bền cắt = 600 MPa. Giải pháp: F = STL t = 4 mm từ Problem 20.4. L = + 50 + 85 25 + 25 + 35 + 25 + 25 + 50 = 320 mm F = 600 (4.0) (320) = 768.000 N. Đây là abou