Energy transfer Ce3+ → Mn2+ in
b-C

Energy transfer Ce3+ → Mn2+ in
b-CaSiO3 (
CaSiO3 for short in this paper) was reported in previous work,and in this host, Mn2+ presents red emission. The luminescence of -CaSiO3:Eu2+ was studied, which gave poor luminescence at room temperature. In a-CaSiO3:Eu2+, the cation Ca3+/Eu2+ forms chains, which would lead to preferential orientation of a d-orbital of Eu2+ along the chain. This characteristic results in long wavelength emission of Eu2+ and strong temperature quenching effect for Eu2+ emission. No research on the luminescence of Eu2+/Mn2+, Ce3+/Eu2+, or Ce3+/Eu2+/Mn2+ codoped CaSiO3 has been reported as far as we know. In this paper,
we investigate the energy transfer among Ce3+/Eu2+/Mn2+ in CaSiO in order to obtain red/orange phosphors for white-light UV-LED applications.

Kết quả (Việt) 1:

Năng lượng chuyển Ce3 + → Mn2 + trong b-CaSiO3 (CaSiO3 cho ngắn trong bài báo này) đã được báo cáo trong công việc trước đó, và trong máy chủ này, Mn2 + quà màu đỏ phát thải. Đây-CaSiO3:Eu2+ đã được nghiên cứu, mà đã cho người nghèo đây ở nhiệt độ phòng. Trong một - CaSiO3:Eu2+, cation Ca3 +/ Eu2 + tạo thành dây chuyền, mà sẽ dẫn đến các định hướng ưu đãi của một d-quỹ đạo của Eu2 + dọc theo dãy. Tính chất này kết quả trong dài bước sóng phát thải của Eu2 + và nhiệt độ mạnh tôi có hiệu lực cho Eu2 + phát thải. Không có nghiên cứu về đây Eu2 +/ Mn2 +, Ce3 +/ Eu2 +, hay Ce3 +/ Eu2 +/ Mn2 + codoped CaSiO3 đã được báo cáo như xa như chúng tôi biết. Trong bài báo này,chúng tôi điều tra việc chuyển giao năng lượng trong số Ce3 +/ Eu2 +/ Mn2 + trong CaSiO để có được màu đỏ/cam phosphors cho ánh sáng trắng đèn LED UV ứng dụng.