Precursor sol solution preparation:

Precursor sol solution preparation:
The precursor solution was prepared by dissolving Cu(CH3COO)2·H2O (0.4 mol/L, AR), Zn(CH3COO)2·2H2O (0.25 mol/L, AR), SnCl2·2H2O (0.2 mol/L, AR) and SC(NH2)2 (1.6 mol/L, AR) into in 2-methoxyethanol (AR) while stirring at 50 ºC for several hours to get dark yellow solution. After aging at room temperature in air for several days, the prepared precursor solution was converted into sol solution and then proper Monoethanolamine (1% molar concentration) was added and stirred to avoid cracks during spin coating. All chemical reagent were purchased from Sinopharm Chemical Reagent Co., ltd.

Kết quả (Việt) 2:

Tiền thân chuẩn bị giải pháp sol:
Các giải pháp tiền thân đã được chuẩn bị bằng cách hòa tan Cu (CH3COO) 2 · H2O (0,4 mol / L, AR), Zn (CH3COO) 2 · 2H2O (0,25 mol / L, AR), SnCl2 · 2H2O (0,2 mol / L, AR) và SC (NH2) 2 (1,6 mol / L, AR) vào trong 2 methoxyethanol (AR) trong khi khuấy ở 50 ºC trong vài giờ để có được dung dịch màu vàng sẫm. Sau khi lão hóa ở nhiệt độ phòng trong không khí trong vài ngày, các giải pháp tiền thân chuẩn bị đã được chuyển đổi thành giải pháp sol và sau đó đúng Monoethanolamine (1% nồng độ mol) được thêm vào và khuấy đều để tránh các vết nứt trong lớp phủ spin. Tất cả các thuốc thử hóa học đã được mua từ Sinopharm hóa chất thuốc thử Co., ltd.