4.1.4.3. Dilute acid pretreatment (

4.1.4.3. Dilute acid pretreatment (DA). Concept: this is method of biomass pretreatment has received extensive research (Mcmillan 1994), both for the possibility of its application as a replacement for enzymatic hydrolysis of cellulose and as a lignocellulosic biomass pretreatment step to enhance biomass digestibility (Lee et al. 1999; Nguyen 2000). As a lignocellulosic biomass pretreatment method, DA pretreatment with high reaction rates and improved cellulose
hydrolysis has been successfully developed for biomass pretreatment while conventional dilute acid based cellulose hydrolysis has become an unpopular concept with little research efforts to revive its use to hydrolyze cellulose (Esteghalian et al. 1997; Sun and Cheng 2002).
Hydrochloric acid, nitric acid, phosphoric acid, and sulfuric acid have been tested for use in biomass pretreatment. Dilute sulfuric acid is commonly used as the acid of choice (Kim et al. 2000; Mosier et al. 2005b; Nguyen 2000; Torget et al. 1992). Dilute sulfuric acid is mixed
with biomass to solubilize hemicellulose therefore increasing the accessibility of the cellulose in the biomass. This mixture can be heated directly with the use of steam as in SP, or indirectly via the vessel walls of the reactor.
Process description and mode of action: an aqueous solution of substrate is heated to the desired temperature and pretreated using preheated sulfuric acid (concentrations of b4 wt.%) in a stainless-steel reactor (Esteghalian et al. 1997; Torget et al. 1990). In this case DA
pretreatment begins upon addition of the acid. DA pretreatment is carried at temperature ranging from 140 to 215 °C. The residence time ranges from a few seconds to minutes depending on the temperature of the pretreatment. In another method preconditioned and physically pretreated biomass in a wire mesh is submerged in a circulating bath of dilute sulfuric acid. The bath is then heated to desired temperatures to effect pretreatment at different severities. A two
stage dilute acid pretreatment to maximize sugar recovery and enhance biomass digestibility was reported by Nguyen (2000). A low severity (low temperature, low acid concentration) DA pretreatment was used in the first stage to promote hemicellulose hydrolysis/ recovery and a high severity second stage was used to hydrolyze a portion of the remaining cellulose to glucose in the second stage (Nguyen 2000).

Kết quả (Việt) 1:

4.1.4.3. pha loãng axít pretreatment (DA). Khái niệm: đây là phương pháp của nhiên liệu sinh học pretreatment đã nhận được nghiên cứu sâu rộng (Mcmillan năm 1994), cả hai đều cho khả năng ứng dụng của nó như là một thay thế cho enzym thủy phân cellulose và như một nhiên liệu sinh học lignocellulo tiền xử lý bước để tăng cường tiêu hóa sinh khối (Lee et al. 1999; Nguyễn năm 2000). Như là một phương pháp tiền xử lý nhiên liệu sinh học lignocellulo, DA pretreatment với tỷ lệ phản ứng cao và cải thiện cellulosethủy phân đã được phát triển thành công cho nhiên liệu sinh học pretreatment trong khi thông thường axít loãng dựa thủy phân cellulose đã trở thành một khái niệm không phổ biến với những nỗ lực nghiên cứu nhỏ để phục hồi sử dụng của nó để hydrolyze cellulose (Esteghalian et al. năm 1997; Sun và Cheng 2002).Axít clohiđric, axít nitric, axit photphoric và axit sulfuric đã được thử nghiệm để sử dụng trong nhiên liệu sinh học pretreatment. Axít sulfuric loãng thường được sử dụng như axit của sự lựa chọn (Kim et al. năm 2000; Mosier et al. 2005b; Nguyễn 2000; Torget et al. 1992). Axít sulfuric loãng hỗn hợpvới nhiên liệu sinh học để solubilize hemicellulose do đó tăng khả năng tiếp cận cellulose trong nhiên liệu sinh học. Hỗn hợp này có thể được đun nóng trực tiếp với việc sử dụng của hơi nước như trong SP, hoặc gián tiếp thông qua các bức tường tàu của lò phản ứng.Xử lý chế độ hành động và mô tả: một giải pháp dung dịch nước của bề mặt được đun nóng đến nhiệt độ mong muốn và sử dụng pretreated preheated axít sulfuric (nồng độ của b4 wt.%) trong một lò phản ứng thép không gỉ (Esteghalian et al. năm 1997; Torget et al. 1990). Trong trường hợp này DApretreatment begins upon addition of the acid. DA pretreatment is carried at temperature ranging from 140 to 215 °C. The residence time ranges from a few seconds to minutes depending on the temperature of the pretreatment. In another method preconditioned and physically pretreated biomass in a wire mesh is submerged in a circulating bath of dilute sulfuric acid. The bath is then heated to desired temperatures to effect pretreatment at different severities. A twostage dilute acid pretreatment to maximize sugar recovery and enhance biomass digestibility was reported by Nguyen (2000). A low severity (low temperature, low acid concentration) DA pretreatment was used in the first stage to promote hemicellulose hydrolysis/ recovery and a high severity second stage was used to hydrolyze a portion of the remaining cellulose to glucose in the second stage (Nguyen 2000).

Kết quả (Việt) 2:

4.1.4.3. Pha loãng trước khi điều trị acid (DA). Khái niệm: đây là phương pháp sinh khối tiền xử lý đã được nghiên cứu sâu rộng (McMillan 1994), cả về khả năng ứng dụng của nó như là một sự thay thế cho thủy phân enzyme cellulose và như là một bước sinh khối tiền xử lý lignocellulose để tăng cường sinh khối tiêu hóa (Lee et al 1999;. Nguyễn 2000). Là một phương pháp tiền xử lý sinh khối lignocellulose, tiền xử lý DA với tốc độ phản ứng cao và cải thiện cellulose
thủy phân đã được phát triển thành công cho sinh khối tiền xử lý trong khi axit loãng thông thường dựa trên cellulose thủy đã trở thành một khái niệm được ưa chuộng với những nỗ lực nghiên cứu nhỏ để làm sống lại việc sử dụng nó để thủy phân cellulose (Esteghalian et . al 1997;. Sun và Cheng 2002)
axit clohydric, axit nitric, axit photphoric và axit sulfuric đã được thử nghiệm để sử dụng trong sinh khối tiền xử lý. Pha loãng axit sulfuric được sử dụng phổ biến như axit của sự lựa chọn (Kim et al 2000;.. Mosier et al 2005b; Nguyễn 2000; Torget et al 1992.). Pha loãng axit sulfuric được trộn
với nhiên liệu sinh học để hòa tan hemicellulose do đó tăng khả năng tiếp cận của cellulose trong sinh khối. Hỗn hợp này có thể được làm nóng trực tiếp với việc sử dụng hơi nước như trong SP, hoặc gián tiếp thông qua các thành mạch của các lò phản ứng.
Mô tả quá trình và phương thức hành động: một dung dịch chất nền được nung nóng tới nhiệt độ mong muốn và xử lý sơ bộ bằng axit sulfuric nóng sẵn ( .. Nồng độ của b4 wt%) trong một lò phản ứng bằng thép không gỉ (Esteghalian et al 1997; Torget et al 1990).. Trong trường hợp này DA
xử lý trước khi bắt đầu bổ sung các axit. DA tiền xử lý được thực hiện ở nhiệt độ khác nhau, 140-215 ° C. Thời gian lưu trú khoảng từ vài giây đến vài phút tùy thuộc vào nhiệt độ của tiền xử lý. Trong một phương pháp điều kiện cư và sinh khối chất xử lý sơ bộ trong một lưới thép chìm trong bồn tắm lưu hành của axit sunfuric loãng. Các phòng tắm được thì nóng tới nhiệt độ mong muốn để thực hiện tiền xử lý ở mức độ nghèo khác nhau. Một hai
giai đoạn axit loãng tiền xử lý để tối đa đường và tăng cường khả năng tiêu hóa sinh khối đã được báo cáo bởi Nguyễn (2000). Một mức độ thấp (nhiệt độ thấp, nồng độ axit thấp) DA tiền xử lý được sử dụng trong giai đoạn đầu tiên để thúc đẩy hemicellulose thủy phân / phục hồi và một giai đoạn thứ hai mức độ cao đã được sử dụng để thủy phân một phần của cellulose còn lại thành glucose trong giai đoạn thứ hai (Nguyen 2000 ).