4. ConclusionThe clinoptilolite and

4. Conclusion

The clinoptilolite and montmorillonite have been synthesized

hydrothermally and also their surfactant modifications have been

made by using HDTMAB and DODMAB surfactants. Various analytical techniques such as XRD, FT-IR, EDS, SEM and TEM are

used to characterize the products. Diffraction studies show that

the materials have good crystalline character with well devel-
oped phases. Morphological studies made in this work indicate

that the as-synthesized clinoptilolite and montmorillonite have

nano size particles. In the present work, the possible use of

SMSs as efficient nitrate adsorbent and as SRFs has also been

investigated. Langmuir and Freundlich isotherm are fitted well

with the experimental nitrate adsorption data. The calculated

Kết quả (Việt) 2:

4. Kết luận Các clinoptilolite và montmorillonite đã được tổng hợp thủy nhiệt và cũng thay đổi bề mặt của họ đã được thực hiện bằng cách sử dụng HDTMAB và DODMAB bề mặt. Kỹ thuật phân tích khác nhau như XRD, FT-IR, EDS, SEM và TEM được sử dụng để mô tả sản phẩm. Nghiên cứu nhiễu xạ cho thấy các vật liệu có tính cách tinh tốt với cũng triển giai đoạn oped. Nghiên cứu hình thái học thực hiện trong công việc này chỉ ra rằng các clinoptilolite như được tổng hợp và montmorillonite có các hạt kích thước nano. Trong công việc hiện tại, khả năng sử dụng tin nhắn SMS như nitrat chất hấp phụ và hiệu quả như SRFs cũng đã được điều tra. Langmuir và Freundlich đường đẳng nhiệt được trang bị tốt với các dữ liệu thực nghiệm nitrate hấp phụ. Các tính toán