for LIBs has been hindered by its h

for LIBs has been hindered by its huge initial capacity loss and severe
capacity fading upon extended cycling. These drawbacks are mainly
caused by the large volume variation accompanied by the chargedischarge
process. Several reports have suggested that creating unique
nanostructured SnO2, such as hollow or mesoporous materials4-6, could
have some positive effect to overcome these shortcomings, where the
introduced void space can accommodate the volume expansion during
the charge-discharge process. Additionally, introduction of carbonaceous
supports, like amorphous carbon, or reduced graphene oxide,7-9 could
also alleviate the abovementioned problems of SnO2 by providing an
elastic matrix which helps to buffer the stress induced during lithium
uptake and release

Kết quả (Việt) 1:

cho LIBs đã bị cản trở bởi mất mát rất lớn công suất ban đầu của nó và nghiêm trọngkhả năng mờ dần khi mở rộng Chạy xe đạp. Những hạn chế chủ yếu làgây ra bởi các biến thể khối lượng lớn đi kèm với chargedischargequá trình. Một số báo cáo đã gợi ý rằng tạo duy nhấttrong SnO2, chẳng hạn như rỗng hoặc mesoporous materials4-6, có thểcó một số hiệu ứng tích cực để khắc phục những thiếu sót, nơi cácgiới thiệu khoảng trống không gian có thể phục vụ mở rộng lượng trongtrình phí xả. Ngoài ra, giới thiệu của carbonatehỗ trợ, như vô định hình cacbon, hoặc giảm graphen ôxít, 7-9 có thểcũng làm giảm bớt những vấn đề trên của SnO2 bằng cách cung cấp mộtma trận đàn hồi giúp để đệm những căng thẳng gây ra trong litihấp thụ và phát hành