Welding: The DIY Guide > TIG Tutorial > Set Up
TIG Welder Set Up

Setup is covered in more detail in the TIG FAQ. The basic information on this page should be a good starting point apart from for specific joints where alternative set up is detailed in the relevant tutorial page.

Tungsten
For welding steel the tungsten should be ground to a long point with the taper length about 2 or 3 times the diameter of the tungsten. See DC Electrode Preparation. The long taper and sharp tip improve arc stability.

For a butt weld or open corner weld the stick out would be about 5-6mm. Setting the tungsten stick out for fillet welds is covered on the fillet weld page.

Gas Shrouds
For general purpose work on steel a number 7 shroud is a good compromise. A smaller number 4 shroud would be more suitable for fillet welds, and larger shrouds might be used for aluminium. As a rule the larger the shroud the better the gas coverage.

Tundsten set to 5-6mm stick out
Shielding Gas
Pure Argon is normally used as a TIG shielding gas and is suitable for both steel and aluminium welding. The shielding gas must be completely inert - MIG shielding gasses cannot be used as the CO2 would cause the tungsten to oxidise.

Flow Rate
Flow rate will generally be 6 to 7L/min. The rate might be increased slightly to compensate for drafty conditions. TIG uses a lot of shielding gas so it pays to set up the gas flow accurately. A flow meter attached to the regulator will give a more accurate flow reading than the gauge on the regulator (see the regulator page for the set up), or a peashooter type flow meter can be used to measure flow at the torch (see the photo to the right).

Post-Flow Time
Postflow protects the tungsten and the weld as they cool. The tungsten will take longer to cool from higher amps, and a rough rule of thumb is to increase post flow time by 1 second for every 10 amps. We've used about 4-5 seconds post flow for everything shown in the tutorial.

Gas flow tester
Polarity
DC TIG Welding is carried out with the torch negative and the work positive. That is also known as DCEN (DC electrode negative) or "straight" polarity for those with older welders.

About two thirds of the heat goes to the positive side or the arc. For TIG the negative torch helps avoid overheating the tungsten.

TIG welding and polarity
Other Settings
The only other setting we have used in the tutorial is slope down (set to 1.5 seconds). This reduces the amps gradually at the end of the weld which helps prevent the formation of a crater. The gas post flow time should be significantly longer than slope down time.

Some expensive TIG welders have an AC option. AC current is used for aluminium, DC for steel.

Many of the other knobs on TIG welders are to do with pulse. We've not used pulse at all in the tutorials and it's best switched off while you get the hang of technique.

Kết quả (Việt) 1:

Nhà MIG TIG Arc sơn diễn đàn Weldequip cửa hàng Tìm kiếmHàn: Hướng dẫn tự làm > Hướng dẫn TIG > Thiết lậpMáy hàn TIG thiết lậpThiết lập được bảo hiểm chi tiết hơn trong TIG FAQ. Thông tin cơ bản về trang này nên là một điểm khởi đầu tốt ngoài cụ thể khớp nơi lựa chọn thiết lập là chi tiết ở trang hướng dẫn có liên quan.VonframHàn thép tungsten nên mặt đất đến một điểm dài với chiều dài côn khoảng 2 hoặc 3 lần đường kính của vonfram. Xem DC điện cực chuẩn bị. Taper dài và nhọn mũi cải thiện sự ổn định hồ quang.Mông hàn hay mở góc Hàn thanh ra sẽ có khoảng 5-6 mm. thiết lập tungsten thanh ra cho các mối hàn phi lê được bao phủ trên trang Hàn phi lê.Khí ShroudsCho mục đích chung công việc trên thép tấm vải liệm số 7 là một sự thỏa hiệp tốt. Một tấm vải liệm số 4 nhỏ sẽ phù hợp hơn cho mối hàn phi lê, và shrouds lớn hơn có thể được sử dụng cho nhôm. Như một quy luật lớn che đậy thì tốt hơn phạm vi bảo hiểm khí.Tundsten đặt thành 5-6mm dính raChe chắn khíArgon tinh khiết thường được sử dụng như một chất khí TIG che chắn và phù hợp cho cả thép và nhôm hàn. Che chắn khí phải hoàn toàn trơ - MIG che chắn khí không thể được sử dụng như các khí CO 2 sẽ gây ra Wolfram để oxidise.Tốc độ dòng chảyFlow rate will generally be 6 to 7L/min. The rate might be increased slightly to compensate for drafty conditions. TIG uses a lot of shielding gas so it pays to set up the gas flow accurately. A flow meter attached to the regulator will give a more accurate flow reading than the gauge on the regulator (see the regulator page for the set up), or a peashooter type flow meter can be used to measure flow at the torch (see the photo to the right).Post-Flow TimePostflow protects the tungsten and the weld as they cool. The tungsten will take longer to cool from higher amps, and a rough rule of thumb is to increase post flow time by 1 second for every 10 amps. We've used about 4-5 seconds post flow for everything shown in the tutorial.Gas flow testerPolarityDC TIG Welding is carried out with the torch negative and the work positive. That is also known as DCEN (DC electrode negative) or "straight" polarity for those with older welders.About two thirds of the heat goes to the positive side or the arc. For TIG the negative torch helps avoid overheating the tungsten.TIG welding and polarityOther SettingsThe only other setting we have used in the tutorial is slope down (set to 1.5 seconds). This reduces the amps gradually at the end of the weld which helps prevent the formation of a crater. The gas post flow time should be significantly longer than slope down time.Some expensive TIG welders have an AC option. AC current is used for aluminium, DC for steel.Many of the other knobs on TIG welders are to do with pulse. We've not used pulse at all in the tutorials and it's best switched off while you get the hang of technique.

Kết quả (Việt) 2:

Trang chủ MIG TIG Arc Sơn Forum Weldequip Cửa hàng

Tìm kiếm
hàn: Hướng dẫn DIY> TIG Tutorial> Set Up
TIG Máy hàn Thiết lập

cài đặt được trình bày chi tiết hơn trong các TIG FAQ. Các thông tin cơ bản trên trang này phải là một điểm khởi đầu tốt ngoài cho khớp cụ thể mà thay thế thiết lập được nêu chi tiết trong trang hướng dẫn có liên quan.

Vonfram
Dùng hàn thép vonfram được nghiền đến một điểm dài với chiều dài côn khoảng 2 hoặc 3 lần đường kính của vonfram. Xem DC điện cực chuẩn bị. Các côn dài và nhọn cải thiện sự ổn định hồ quang.

Đối với một mối hàn mông hoặc góc mở hàn các thanh ra sẽ vào khoảng 5-6mm. Thiết lập các thanh vonfram ra cho mối hàn phi lê được bao phủ trên trang fillet hàn.

Gas chằng
Đối với công việc mục đích chung về thép tấm vải liệm số 7 là một sự thỏa hiệp tốt. Một số nhỏ hơn 4 liệm sẽ là phù hợp hơn cho các mối hàn phi lê, và những tấm vải liệm lớn hơn có thể được sử dụng cho nhôm. Như một quy luật lớn hơn tấm vải liệm tốt hơn vùng phủ sóng khí.

Tundsten thiết lập để 5-6mm dính ra
che chắn khí
tinh khiết Argon thường được sử dụng như một loại khí che chắn TIG và phù hợp cho cả hai loại thép và hàn nhôm. Các khí che chắn phải được hoàn toàn trơ - MIG che chắn khí không thể được sử dụng như là CO2 sẽ gây ra vonfram để oxy hoá.

Lưu lượng
Lưu lượng nói chung sẽ được 6 đến 7L / phút. Tỷ lệ có thể được tăng lên một chút để bù đắp cho điều kiện gió lùa. TIG sử dụng rất nhiều khí bảo vệ để nó trả tiền để thiết lập các dòng khí chính xác. Một đo lưu lượng gắn liền với các điều chỉnh sẽ cung cấp cho một dòng chảy chính xác hơn đọc hơn đồng hồ đo trên bộ điều chỉnh (xem trang điều cho các thiết lập), hoặc một mét loại peashooter dòng chảy có thể được sử dụng để đo dòng chảy ở ngọn đuốc (xem ảnh bên phải).

bài-Flow Time
Postflow bảo vệ vonfram và các mối hàn khi làm nguội. Các vonfram sẽ mất nhiều thời gian để làm mát từ amps cao hơn, và một quy tắc thô của ngón tay cái là để tăng thời gian lưu bài 1 giây cho mỗi 10 amps. Chúng tôi đã sử dụng khoảng 4-5 giây gửi lưu lượng cho tất cả mọi thứ như trong hướng dẫn.

Dòng khí thử
phân cực
DC TIG được thực hiện với ngọn đuốc tiêu cực và làm việc tích cực. Đó cũng được biết đến như DCEN (DC điện cực âm) hoặc cực "thẳng" đối với những người thợ lớn tuổi.

Khoảng hai phần ba số nhiệt đi vào mặt tích cực hoặc vòng cung. Đối với TIG ngọn đuốc âm giúp tránh quá nhiệt vonfram.

Hàn TIG và cực
Cài đặt khác
Các chỉ thiết lập khác mà chúng tôi đã sử dụng trong hướng dẫn này là dốc xuống (thiết lập để 1,5 giây). Điều này làm giảm amps dần vào cuối mối hàn giúp ngăn ngừa sự hình thành của một miệng núi lửa. Các bài khí dòng chảy thời gian nên dài hơn đáng kể hơn so với độ dốc xuống thời gian.

Một số thợ hàn TIG đắt có một tùy chọn AC. AC hiện tại được sử dụng cho nhôm, DC cho thép.

Nhiều người trong số các nút bấm khác trên thợ hàn TIG là để làm với xung. Chúng tôi đã không được sử dụng ở tất cả các xung trong các bài hướng dẫn và nó tốt nhất tắt trong khi bạn nhận được hang của kỹ thuật.