Hence, in the present study mesopor

Hence, in the present study mesoporous monometallic
Cr-MCM-41(Si/Cr 25, 50, 75 and 100), Fe-MCM-41(Si/Fe=25) and
bimetallic Cr-Fe-MCM-41(Si/(Cr+Fe)=100) molecular sieves were
synthesized by direct hydrothermal method (DHT). The materials were
iv
characterized by various physico-chemical techniques such as XRD,
ICP-AES, Nitrogen adsorption–desorption isotherms, DR-UV–Vis
spectroscopy, EPR spectroscopy and SEM techniques. The chromium and
iron contents in Cr-MCM-41, Fe-MCM-41 and Cr-Fe-MCM-41 are
determined using ICP-AES techniques. From the XRD data the mesoporous
nature of the synthesized catalyst is clearly evident. The long-range regularity
of hexagonal arrays of mesopores of MCM-41 is evident from the intensity of
diffraction peaks. Typical type IV isotherm as defined by IUPAC for

Kết quả (Việt) 2:

Do đó, trong nghiên cứu chế độ độc kim mao
Cr-MCM-41 (Si / Cr 25, 50, 75 và 100), Fe-MCM-41 (Si / Fe = 25) và
lưỡng kim Cr-Fe-MCM-41 (Si / (Cr + Fe) = 100) rây phân tử được
tổng hợp bằng phương pháp thủy nhiệt trực tiếp (DHT). Các tài liệu đã được
iv
đặc trưng bởi các kỹ thuật hóa lý khác nhau như XRD,
ICP-AES, Nitơ isotherms hấp phụ-giải hấp, DR-UV-Vis
quang phổ, quang phổ kế EPR và kỹ thuật SEM. Crom và
nội dung sắt trong Cr-MCM-41, Fe-MCM-41 và Cr-Fe-MCM-41 được
xác định bằng kỹ thuật ICP-AES. Từ các dữ liệu XRD các mao
bản chất của các chất xúc tác tổng hợp rõ ràng là điều hiển nhiên. Đều đặn tầm xa
của các mảng lục giác của mesopores của MCM-41 là bằng chứng từ các cường độ
đỉnh nhiễu xạ. Điển hình đường đẳng nhiệt loại IV theo định nghĩa của IUPAC cho