Of particular interest is the effec

Of particular interest is the effect of slag cement when
concrete is tested for flexural strength (modulus of rupture).
When comparisons are made between concrete with and
without slag cement, where the slag cement is used at proportions designed for greatest strength, the blends generally yield
higher modulus of rupture at ages beyond 7 days (Fulton
1974; Malhotra 1980; Hogan and Meusel 1981) (Fig. 5.5).
This is believed to be a result of the increased density of the
paste and improved bond at the aggregate-paste interface.
Early studies on flexural strength were conducted with
Type IS blended cements. Klieger and Isberner (1967) found
essentially the same flexural strength in concrete containing
portland blast-furnace slag cement as compared with Type I
portland-cement concrete. Stutterheim, as quoted by Fulton
(1974), also confirmed this using concrete containing equal
amounts of slag cement and portland cement and concrete
with portland cement only.

Kết quả (Việt) 1:

Quan tâm đặc biệt là tác dụng của xỉ xi măng khibê tông thử nghiệm sức mạnh flexural (mô đun vỡ).Khi so sánh được thực hiện giữa bê tông với vàmà không có xi măng xỉ, nơi mà xi măng xỉ được sử dụng tại tỷ lệ được thiết kế cho sức mạnh lớn nhất, hỗn hợp thường mang lạiCác mô đun cao của vỡ ở các lứa tuổi vượt quá 7 ngày (Fultonnăm 1974; Malhotra 1980; Hogan và Meusel 1981) (hình 5.5).Điều này được cho là kết quả của mật độ gia tăng của cácdán và các trái phiếu được cải tiến giao diện tổng hợp-dán.Các nghiên cứu ban đầu về sức mạnh flexural đã được tiến hành vớiLoại IS pha trộn xi măng. Klieger và Isberner (1967) được tìm thấyvề cơ bản giống nhau flexural sức mạnh trong bê tông có chứaPortland vụ nổ lò xỉ xi măng khi so sánh với loại Ibê tông xi măng Portland. Stutterheim, như là trích dẫn của FultonMê-hi-cô (1974), cũng khẳng định điều này bằng cách sử dụng có chứa bằng bê tôngsố tiền của xỉ xi măng và xi măng và bê tôngvới xi măng portland chỉ.